Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT/PC V3900WX-BK1H078 SABIC INNOVATIVE SHANGHAI
VALOX™
Automotive sector、Charging station、Electronic and electrical、Lighting applications、Communication equipment、Wire and cable
High impact、Low warpage、Dimensional stability、High toughness、Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/PC/SABIC INNOVATIVE SHANGHAI/V3900WX-BK1H078
density
ISO1183
g/cm³
1
density
ASTMD792
g/cm³
1
Melt Volume-Flow Rate (MVR)
265°C/2.16kg
ISO1133
cm3/10min
9
Melt mass flow rate
265°C/2.16kg
ASTMD1238
g/10min
1
Shrinkage rate
MD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/PC/SABIC INNOVATIVE SHANGHAI/V3900WX-BK1H078
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
5
Tensile modulus
ISO527-2/1
Mpa
2
Tensile modulus
ASTMD638
Mpa
2
tensile strength
屈服
内部方法
Mpa
4
tensile strength
屈服
ASTMD638
Mpa
5
tensile strength
屈服
ISO527-2/50
Mpa
5
tensile strength
断裂
ASTMD638
Mpa
4
tensile strength
断裂
ISO527-2/50
Mpa
4
elongation
屈服
ASTMD638
%
5
elongation
屈服
ISO527-2/50
%
4
elongation
断裂
内部方法
%
2
elongation
断裂3
ASTMD638
%
5
elongation
断裂
ISO527-2/50
%
4
Bending modulus
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
bending strength
ISO178
Mpa
7
bending strength
屈服,50.0mm跨距
ASTMD790
Mpa
8
Impact strength of cantilever beam gap
-30°C
ASTMD256
J/m
1
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
8
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
8
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
4
Dart impact equipped with measuring instruments
-40°C,TotalEnergy
ASTMD3763
J
5
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
5
Thermal performance
Test Condition
Test Method
Unit
PBT/PC/SABIC INNOVATIVE SHANGHAI/V3900WX-BK1H078
RTI Elec
UL746
°C
1
RTI Imp
UL746
°C
1
RTI Str
UL746
°C
1
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
7
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
9
Hot deformation temperature
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
7
vicat softening point
ASTMD152510
°C
1
vicat softening point
--
ISO306/B50
°C
1
vicat softening point
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
8
Linear coefficient of thermal expansion
MD：-40到40°C
ISO11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
9
Linear coefficient of thermal expansion
TD：-40到40°C
ISO11359-2
cm/cm/°C
9
Electrical performance
Test Condition
Test Method
Unit
PBT/PC/SABIC INNOVATIVE SHANGHAI/V3900WX-BK1H078
Surface resistivity
ASTMD257
ohms
6
flammability
Test Condition
Test Method
Unit
PBT/PC/SABIC INNOVATIVE SHANGHAI/V3900WX-BK1H078
Hot filament ignition temperature
1.0mm
IEC60695-2-13
°C
8
Hot filament ignition temperature
3.0mm
IEC60695-2-13
°C
7
Burning wire flammability index
1.0mm
IEC60695-2-12
°C
9
Burning wire flammability index
3.0mm11
IEC60695-2-12
°C
9