PC/PET XYLEX™ X8300MR BK1D168 SABIC INNOVATIVE US
253
Unit Price:$2448 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 42MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant｜High heat resistance
- Application Areas:Automotive Applications｜Electronic and electrical
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 265°C/2.16 kg | ASTM D1238 | 15 g/10 min |
| Melt Volume flow Rate | 265°C/2.16 kg | ISO 1133 | 15.0 cm3/10min |
| Modeling Shrinkage | 流动 : 3.20 mm | 内部方法 | 0.50 到 0.80 % |
| 横向流动 : 3.20 mm | 内部方法 | 0.40 到 0.60 % | |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.050 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.20 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 79.0 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 75.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9 | ISO 75-2/Ae | 80.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8 | ISO 75-2/Af | 78.0 °C | |
| Vicat Softening Temperature | -- | ASTM D152510 | 91.0 °C |
| -- | ISO 306/B120 | 96.0 °C | |
| Ball PressureTest | 85°C | IEC 60695-10-2 | 通过 |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 1.1E-4 cm/cm/°C |
| 流动 : 23 到 60°C | ISO 11359-2 | 9.0E-5 cm/cm/°C | |
| 横向 : -40 到 40°C | ASTM E831 | 1.1E-4 cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 1.1E-4 cm/cm/°C | |
| 横向 : 23 到 60°C | ISO 11359-2 | 9.0E-5 cm/cm/°C | |
| Thermal Conductivity | ISO 8302 | 0.23 W/m/K |
| Optical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Index of Refraction | ISO 489 | 1.539 | |
| Transmittance | 2540 µm | ASTM D1003 | 88.0 % |
| Haze | 2540 µm | ASTM D1003 | 1.0 % |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | V-2 |
| Glow Wire Flammability Index | 1.0 mm | IEC 60695-2-12 | 750 °C |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | -- 2 | ASTM D638 | 1520 Mpa |
| -- | ISO 527-2/1 | 1600 Mpa | |
| Tensile Strength | 屈服 3 | ASTM D638 | 47.0 Mpa |
| 屈服 | ISO 527-2/50 | 55.0 Mpa | |
| 断裂 3 | ASTM D638 | 46.0 Mpa | |
| 断裂 | ISO 527-2/50 | 54.0 Mpa | |
| Tensile Elongation | 屈服 3 | ASTM D638 | 5.0 % |
| 屈服 | ISO 527-2/50 | > 5.0 % | |
| 断裂 3 | ASTM D638 | 150 % | |
| 断裂 | ISO 527-2/50 | > 200 % | |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 1680 Mpa |
| -- 5 | ISO 178 | 1700 Mpa | |
| Flexural Stress | -- 5, 6 | ISO 178 | 78.0 Mpa |
| 屈服, 50.0 mm 跨距 4 | ASTM D790 | 71.0 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms | |
| Volume Resistivity | ASTM D257 | > 1.0E+15 ohms·cm | |
| Comparative Tracking Index | UL 746 | PLC 0 |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 65 到 75 °C | ||
| Drying Time | 3.0 到 5.0 hr | ||
| Suggested Max Moisture | 0.020 % | ||
| Suggested Shot Size | 40 到 80 % | ||
| Rear Temperature | 240 到 250 °C | ||
| Middle Temperature | 240 到 260 °C | ||
| Front Temperature | 245 到 265 °C | ||
| Nozzle Temperature | 245 到 265 °C | ||
| Processing (Melt) Temp | 245 到 265 °C | ||
| Mold Temperature | 45 到 60 °C | ||
| Back Pressure | 0.200 到 0.500 Mpa | ||
| Screw Speed | 20 到 100 rpm | ||
| Vent Depth | 0.013 到 0.020 mm |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore Hardness | 邵氏 D, 10 秒 | ASTM D2240 | 73 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 95.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.