Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PET X8300MR BK1D168 SABIC INNOVATIVE US
XYLEX™ 
Automotive Applications、Electronic and electrical
Flame retardant、High heat resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Thermal PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/X8300MR BK1D168
Thermal ConductivityISO 83020.23 W/m/K
Deflection Temperature Under Load?1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9ISO 75-2/Ae80.0 °C
Linear thermal expansion coefficient横向 : -40 到 40°CASTM E8311.1E-4 cm/cm/°C
Vicat Softening Temperature--ASTM D15251091.0 °C
ISO 306/B12096.0 °C
Linear thermal expansion coefficient横向 : 23 到 60°CISO 11359-29.0E-5 cm/cm/°C
流动 : -40 到 40°CASTM E831, ISO 11359-21.1E-4 cm/cm/°C
流动 : 23 到 60°CISO 11359-29.0E-5 cm/cm/°C
Ball PressureTest85°CIEC 60695-10-2通过
Linear thermal expansion coefficient横向 : -40°CISO 11359-21.1E-4 cm/cm/°C
Deflection Temperature Under Load?1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8ISO 75-2/Af78.0 °C
1.8 MPa, 未退火, 3.20 mmASTM D64875.0 °C
0.45 MPa, 未退火, 3.20 mm79.0 °C
HardnessTest ConditionTest MethodSABIC INNOVATIVE US/X8300MR BK1D168
Shore Hardness邵氏 D, 10 秒ASTM D224073
InjectionTest ConditionTest MethodSABIC INNOVATIVE US/X8300MR BK1D168
Middle Temperature240 到 260 °C
Drying Time3.0 到 5.0 hr
Suggested Shot Size40 到 80 %
Drying Temperature65 到 75 °C
Mold Temperature45 到 60 °C
Vent Depth0.013 到 0.020 mm
Suggested Max Moisture0.020 %
Processing (Melt) Temp245 到 265 °C
Rear Temperature240 到 250 °C
Nozzle Temperature245 到 265 °C
Front Temperature245 到 265 °C
Back Pressure0.200 到 0.500 Mpa
Screw Speed20 到 100 rpm
PhysicalTest ConditionTest MethodSABIC INNOVATIVE US/X8300MR BK1D168
Melt Mass-Flow Rate265°C/2.16 kgASTM D123815 g/10 min
Moisture Absorption平衡, 23°C, 50% RHISO 620.20 %
Melt Volume flow Rate265°C/2.16 kgISO 113315.0 cm3/10min
Modeling Shrinkage横向流动 : 3.20 mm内部方法0.40 到 0.60 %
流动 : 3.20 mm0.50 到 0.80 %
Moisture Absorption饱和, 23°CISO 620.050 %
Mechanical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/X8300MR BK1D168
Tensile Strength断裂ISO 527-2/5054.0 Mpa
Tensile Modulus--ISO 527-2/11600 Mpa
Tensile Elongation断裂 3ASTM D638150 %
Tensile Strength屈服 347.0 Mpa
Tensile Elongation屈服ISO 527-2/50> 5.0 %
Flexural Modulus50.0 mm 跨距 4ASTM D7901680 Mpa
Tensile Modulus-- 2ASTM D6381520 Mpa
Tensile Strength屈服ISO 527-2/5055.0 Mpa
Flexural Stress屈服, 50.0 mm 跨距 4ASTM D79071.0 Mpa
Tensile Elongation屈服 3ASTM D6385.0 %
Flexural Stress-- 5, 6ISO 17878.0 Mpa
Flexural Modulus-- 51700 Mpa
Tensile Elongation断裂ISO 527-2/50> 200 %
Tensile Strength断裂 3ASTM D63846.0 Mpa
OpticalTest ConditionTest MethodSABIC INNOVATIVE US/X8300MR BK1D168
Haze2540 µmASTM D10031.0 %
Index of RefractionISO 4891.539
Transmittance2540 µmASTM D100388.0 %
Impact PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/X8300MR BK1D168
Instrumented Dart Impact23°C, Total EnergyASTM D376395.0 J
FlammabilityTest ConditionTest MethodSABIC INNOVATIVE US/X8300MR BK1D168
UL flame retardant rating3.0 mmUL 94V-2
Glow Wire Flammability Index1.0 mmIEC 60695-2-12750 °C
Electrical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/X8300MR BK1D168
Volume ResistivityASTM D257> 1.0E+15 ohms·cm
Surface Resistivity> 1.0E+15 ohms
Comparative Tracking IndexUL 746PLC 0