PC/PBT VALOX™ 357-OR5G1016 SABIC INNOVATIVE NANSHA
160
- Unit Price:$4043 USD/MT
- Packaging Specification:25 KG/PKG
- Supply Quantity:43MT
- Delivery Terms:FOB
- Port of Loading:China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Impact modification
- Application Areas:Electrical field｜Electronic field｜Architectural application｜Outdoor applications｜Electrical appliances｜Engine hood parts｜Medical supplies｜Nursing supplies｜Plastic bag｜Casters｜Lawn equipment｜Garden equipment｜Household goods｜Liquid handling｜Petroleum Applications｜Natural gas supplies｜Industrial applications｜Spool｜Shell｜switch
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Modeling Shrinkage | TD：--3 | 内部方法 | 1.2to1.6 % |
| Moisture Absorption | 24hr | ASTMD570 | 0.080 % |
| 饱和,23°C | ISO62 | 0.50 % | |
| 平衡,23°C,50%RH | ISO62 | 0.15 % | |
| Outdoor Suitability | UL746C | f2 | |
| Density / Specific Gravity | ASTMD792 | 1.35 g/cm³ | |
| Specific Volume | ASTMD792 | 0.740 cm³/g | |
| Density / Specific Gravity | ISO1183 | 1.34 g/cm³ | |
| Melt Mass-Flow Rate | 250°C/5.0kg | ASTMD1238 | 9.6 g/10min |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 8.00 cm3/10min |
| Modeling Shrinkage | MD：--2 | 内部方法 | 0.80to1.1 % |
| MD：--3 | 内部方法 | 1.0to1.4 % | |
| MD：3.20mm | 内部方法 | 1.0to1.4 % | |
| TD：--2 | 内部方法 | 0.90to1.3 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 135 °C |
| 0.45MPa,未退火,6.40mm | ASTMD648 | 138 °C | |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 98.0 °C | |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 99.0 °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 84.0 °C | |
| Vicat Softening Temperature | ASTMD152513 | 134 °C | |
| -- | ISO306/B50 | 145 °C | |
| -- | ISO306/B120 | 150 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 9.2E-05 cm/cm/°C |
| MD：60to138°C | ASTME831 | 1.2E-04 cm/cm/°C | |
| MD：-40到40°C | ISO11359-2 | 7.2E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 8.4E-05 cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 8.4E-05 cm/cm/°C | |
| RTIElec | UL746 | 120 °C | |
| Evolution Calendar intelligent importer | UL746 | 120 °C | |
| RTIStr | UL746 | 140 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 0.46mm | UL94 | HB |
| 0.63mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | |
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 775 °C |
| 2.0mm | IEC60695-2-13 | 750 °C | |
| 3.0mm | IEC60695-2-13 | 725 °C | |
| Oxygen Index | ASTMD2863 | 30 % |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Stress | 断裂 | ISO527-2/50 | 40.0 Mpa |
| Tensile Strain | Yield | ASTMD638 | 5.0 % |
| 屈服 | ISO527-2/50 | 5.0 % | |
| Break | ASTMD638 | 54 % | |
| 断裂 | ISO527-2/50 | 30 % | |
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2100 Mpa |
| ISO178 | 2000 Mpa | ||
| Flexural Strength | ISO178 | 73.0 Mpa | |
| 屈服,50.0mm跨距 | ASTMD790 | 78.0 Mpa | |
| Break,50.0mmSpan | ASTMD790 | 78.0 Mpa | |
| Tensile Modulus | ASTMD638 | 2020 Mpa | |
| ISO527-2/1 | 2200 Mpa | ||
| Tensile Strength | 屈服 | ASTMD638 | 48.0 Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 50.0 Mpa |
| Tensile Strength | Break | ASTMD638 | 42.0 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume Resistivity | ASTMD257 | >1.2E+16 ohms·cm | |
| Dielectric Strength | 1.60mm,在油中 | ASTMD149 | 25 KV/mm |
| 3.20mm,inAir | ASTMD149 | 19 KV/mm | |
| 3.20mm,在油中 | ASTMD149 | 19 KV/mm | |
| Dielectric Constant | 100Hz | ASTMD150 | 3.20 |
| 1MHz | ASTMD150 | 3.20 | |
| Dissipation Factor? | 100Hz | ASTMD150 | 3E-03 |
| 1MHz | ASTMD150 | 0.030 | |
| Arc Resistance | ASTMD495 | PLC6 | |
| Comparative Tracking Index | CTI | UL746 | PLC 2 |
| High Amp Arc Ignition | HAI | UL746 | PLC 3 |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC 3 |
| Hot-wire Ignition | HWI | UL746 | PLC 2 |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | R级 | ASTMD785 | 117 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| CharpyNotchedImpactStrength9 | 23°C | ISO179/1eA | 45 kJ/m² |
| Notched Izod Impact Strength | -30°C | ASTMD256 | 150 J/m |
| 23°C | ASTMD256 | 320 J/m | |
| -30°C | ISO180/1A | 10 kJ/m² | |
| 23°C | ISO180/1A | 45 kJ/m² | |
| 23°C | ASTMD4812 | NoBreak | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 35.8 J |
| Gardner Impact | 23°C | ASTMD3029 | 43.4 J |
| 23°C11 | ASTMD3029 | 43.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.