Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT 357-OR5G1016 SABIC INNOVATIVE NANSHA
VALOX™
Electrical field、Electronic field、Architectural application、Outdoor applications、Electrical appliances、Engine hood parts、Medical supplies、Nursing supplies、Plastic bag、Casters、Lawn equipment、Garden equipment、Household goods、Liquid handling、Petroleum Applications、Natural gas supplies、Industrial applications、Spool、Shell、switch
Impact modification
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/357-OR5G1016 |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 8.4E-05 cm/cm/°C |
| RTIElec | UL746 | 120 °C | |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 9.2E-05 cm/cm/°C |
| MD：-40到40°C | ISO11359-2 | 7.2E-05 cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 98.0 °C |
| RTIStr | UL746 | 140 °C | |
| Vicat Softening Temperature | -- | ISO306/B120 | 150 °C |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 138 °C |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 99.0 °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 84.0 °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 145 °C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 135 °C |
| Vicat Softening Temperature | ASTMD152513 | 134 °C | |
| Linear thermal expansion coefficient | MD：60to138°C | ASTME831 | 1.2E-04 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 8.4E-05 cm/cm/°C | |
| Evolution Calendar intelligent importer | UL746 | 120 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/357-OR5G1016 |
|---|---|---|---|
| Rockwell Hardness | R级 | ASTMD785 | 117 |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/357-OR5G1016 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2100 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 40.0 Mpa |
| Tensile Strain | 断裂 | ISO527-2/50 | 30 % |
| Tensile Modulus | ISO527-2/1 | 2200 Mpa | |
| Tensile Strain | Break | ASTMD638 | 54 % |
| Tensile Strength | 屈服 | ASTMD638 | 48.0 Mpa |
| Flexural Modulus | ISO178 | 2000 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 78.0 Mpa |
| Tensile Strain | Yield | ASTMD638 | 5.0 % |
| Flexural Strength | Break,50.0mmSpan | ASTMD790 | 78.0 Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 50.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/50 | 5.0 % |
| Flexural Strength | ISO178 | 73.0 Mpa | |
| Tensile Modulus | ASTMD638 | 2020 Mpa | |
| Tensile Strength | Break | ASTMD638 | 42.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/357-OR5G1016 |
|---|---|---|---|
| Outdoor Suitability | UL746C | f2 | |
| Density / Specific Gravity | ASTMD792 | 1.35 g/cm³ | |
| Melt Mass-Flow Rate | 250°C/5.0kg | ASTMD1238 | 9.6 g/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 1.0to1.4 % |
| Specific Volume | ASTMD792 | 0.740 cm³/g | |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.50 % |
| Modeling Shrinkage | MD：--2 | 内部方法 | 0.80to1.1 % |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Density / Specific Gravity | ISO1183 | 1.34 g/cm³ | |
| Moisture Absorption | 24hr | ASTMD570 | 0.080 % |
| Modeling Shrinkage | MD：--3 | 内部方法 | 1.0to1.4 % |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 8.00 cm3/10min |
| Modeling Shrinkage | TD：--2 | 内部方法 | 0.90to1.3 % |
| TD：--3 | 内部方法 | 1.2to1.6 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/357-OR5G1016 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 kJ/m² |
| 23°C | ASTMD4812 | NoBreak | |
| 23°C | ASTMD256 | 320 J/m | |
| Gardner Impact | 23°C | ASTMD3029 | 43.4 J |
| 23°C11 | ASTMD3029 | 43.0 J | |
| Notched Izod Impact Strength | -30°C | ASTMD256 | 150 J/m |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 35.8 J |
| 23°C | ISO179/1eA | 45 kJ/m² | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 45 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/357-OR5G1016 |
|---|---|---|---|
| Flame Rating | 0.63mm | UL94 | V-0 |
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 775 °C |
| Oxygen Index | ASTMD2863 | 30 % | |
| Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 725 °C |
| Flame Rating | 0.46mm | UL94 | HB |
| 3.0mm | UL94 | 5VA | |
| Glow Wire Ignition Temperature | 2.0mm | IEC60695-2-13 | 750 °C |
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 960 °C |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/357-OR5G1016 |
|---|---|---|---|
| Dissipation Factor? | 100Hz | ASTMD150 | 3E-03 |
| 1MHz | ASTMD150 | 0.030 | |
| Arc Resistance | ASTMD495 | PLC6 | |
| Dielectric Constant | 1MHz | ASTMD150 | 3.20 |
| Comparative Tracking Index | CTI | UL746 | PLC 2 |
| High Amp Arc Ignition | HAI | UL746 | PLC 3 |
| Dielectric Strength | 3.20mm,在油中 | ASTMD149 | 19 KV/mm |
| Volume Resistivity | ASTMD257 | >1.2E+16 ohms·cm | |
| Dielectric Constant | 100Hz | ASTMD150 | 3.20 |
| Hot-wire Ignition | HWI | UL746 | PLC 2 |
| Dielectric Strength | 1.60mm,在油中 | ASTMD149 | 25 KV/mm |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC 3 |
| Dielectric Strength | 3.20mm,inAir | ASTMD149 | 19 KV/mm |