PPO NORYL™ HS2000X SABIC INNOVATIVE US
184
- Unit Price:$4483 USD/MT
- Packaging Specification:25 KG/PKG
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading:China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber mineral reinf
- Application Areas:medical care
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Density / Specific Gravity | ASTMD792 | 1.25 g/cm³ | |
| Melt Mass-Flow Rate | 280°C/5.0kg | ASTMD1238 | 7.6 g/10min |
| 300°C/5.0kg | ASTMD1238 | 7.6 g/10min | |
| Melt Volume flow Rate | 280°C/5.0kg | ISO1133 | 6.80 cm3/10min |
| 300°C/5.0kg | ISO1133 | 6.80 cm3/10min | |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50到0.70 % |
| Outdoor Suitability | UL746C | f1 |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Evolution Calendar intelligent importer | UL746 | 85.0 °C | |
| RTI | UL746 | 100 °C | |
| 0.45MPa, Unannealed,3.20mm | ASTMD648 | 117 °C | |
| 0.45MPa, Unannealed,6.40mm | ASTMD648 | 128 °C | |
| 0.45MPa, Unannealed,100mm Span | ISO75-2/Be | 126 °C | |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 108 °C | |
| 1.8MPa, Unannealed,6.40mm | ASTMD648 | 116 °C | |
| 1.8MPa, Unannealed,100mm Span | ISO75-2/Ae | 111 °C | |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831 | 7.1E-05 cm/cm/°C |
| TD:-40到40°C | ASTME831 | 7.8E-05 cm/cm/°C | |
| RTIElec | UL746 | 100 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 1.47mm | UL94 | V-0 |
| 2.01mm | UL94 | 5VA | |
| RadiantPanelListing(UL) | UL94 | YES |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| yield | ISO527-2 | 71.7 Mpa | |
| Break | ASTMD638 | 60.0 Mpa | |
| fracture | ISO527-2 | 57.1 Mpa | |
| yield | ASTMD638 | 3.8 % | |
| ISO527-2 | 3.7 % | ||
| Break | ASTMD638 | 8.4 % | |
| fracture | ISO527-2 | 11 % | |
| 100mm Span | ASTMD790 | 3550 Mpa | |
| 50.0mm Span | ASTMD790 | 3670 Mpa | |
| --1 | ASTMD638 | 3650 Mpa | |
| Yield | ASTMD638 | 74.0 Mpa | |
| Yield,100mm Span | ASTMD790 | 117 Mpa | |
| Break,50.0mm Span | ASTMD790 | 117 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTMD257 | >1.0E+16 ohms | |
| Volume Resistivity | ASTMD257 | 1.2E+16 ohms·cm | |
| Dielectric Strength | 3.20mm,inOil | ASTMD149 | 17 KV/mm |
| Dielectric Constant | 50Hz | ASTMD150 | 2.89 |
| 60Hz | ASTMD150 | 2.89 | |
| 1MHz | ASTMD150 | 2.70 | |
| Dissipation Factor? | 50Hz | ASTMD150 | 0.017 |
| 60Hz | ASTMD150 | 0.017 | |
| 1MHz | ASTMD150 | 4.4E-03 | |
| Arc Resistance | ASTMD495 | PLC6 | |
| Comparative Tracking Index | CTI | UL746 | PLC 2 |
| High Amp Arc Ignition | HAI | UL746 | PLC 2 |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC 3 |
| Hot-wire Ignition | HWI | UL746 | PLC 0 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/2C | 10 kJ/m² |
| 23°C | ASTMD256 | 130 J/m | |
| 23°C9 | ISO180/1A | 9.7 kJ/m² | |
| Unnotched Izod Impact Strength | 23°C | ASTMD4812 | 2200 J/m |
| Reverse Notch Izod Impact | 3.20mm | ASTMD256 | 810 J/m |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 443 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.