Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO HS2000X SABIC INNOVATIVE US
NORYL™
medical care
Glass fiber mineral reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HS2000X |
|---|---|---|---|
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 108 °C | |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831 | 7.1E-05 cm/cm/°C |
| RTIElec | UL746 | 100 °C | |
| RTI | UL746 | 100 °C | |
| 0.45MPa, Unannealed,3.20mm | ASTMD648 | 117 °C | |
| 0.45MPa, Unannealed,6.40mm | ASTMD648 | 128 °C | |
| 0.45MPa, Unannealed,100mm Span | ISO75-2/Be | 126 °C | |
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831 | 7.8E-05 cm/cm/°C |
| Evolution Calendar intelligent importer | UL746 | 85.0 °C | |
| 1.8MPa, Unannealed,100mm Span | ISO75-2/Ae | 111 °C | |
| 1.8MPa, Unannealed,6.40mm | ASTMD648 | 116 °C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HS2000X |
|---|---|---|---|
| Break | ASTMD638 | 60.0 Mpa | |
| Yield,100mm Span | ASTMD790 | 117 Mpa | |
| fracture | ISO527-2 | 57.1 Mpa | |
| 100mm Span | ASTMD790 | 3550 Mpa | |
| yield | ISO527-2 | 3.7 % | |
| Break,50.0mm Span | ASTMD790 | 117 Mpa | |
| ASTMD638 | 3650 Mpa | ||
| Break | ASTMD638 | 8.4 % | |
| yield | ASTMD638 | 3.8 % | |
| fracture | ISO527-2 | 11 % | |
| yield | ISO527-2 | 71.7 Mpa | |
| 50.0mm Span | ASTMD790 | 3670 Mpa | |
| Yield | ASTMD638 | 74.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/HS2000X |
|---|---|---|---|
| Outdoor Suitability | UL746C | f1 | |
| Density / Specific Gravity | ASTMD792 | 1.25 g/cm³ | |
| Melt Volume flow Rate | 300°C/5.0kg | ISO1133 | 6.80 cm3/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50到0.70 % |
| Melt Mass-Flow Rate | 300°C/5.0kg | ASTMD1238 | 7.6 g/10min |
| Melt Volume flow Rate | 280°C/5.0kg | ISO1133 | 6.80 cm3/10min |
| Melt Mass-Flow Rate | 280°C/5.0kg | ASTMD1238 | 7.6 g/10min |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HS2000X |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/2C | 10 kJ/m² |
| Reverse Notch Izod Impact | 3.20mm | ASTMD256 | 810 J/m |
| ASTMD256 | 130 J/m | ||
| ISO180/1A | 9.7 kJ/m² | ||
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 443 J |
| Unnotched Izod Impact Strength | 23°C | ASTMD4812 | 2200 J/m |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/HS2000X |
|---|---|---|---|
| Flame Rating | 2.01mm | UL94 | 5VA |
| 1.47mm | UL94 | V-0 | |
| RadiantPanelListing(UL) | UL94 | YES |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HS2000X |
|---|---|---|---|
| Dielectric Constant | 60Hz | ASTMD150 | 2.89 |
| Surface Resistivity | ASTMD257 | >1.0E+16 ohms | |
| Dielectric Constant | 50Hz | ASTMD150 | 2.89 |
| Dissipation Factor? | 50Hz | ASTMD150 | 0.017 |
| 60Hz | ASTMD150 | 0.017 | |
| 1MHz | ASTMD150 | 4.4E-03 | |
| Arc Resistance | ASTMD495 | PLC6 | |
| Dielectric Constant | 1MHz | ASTMD150 | 2.70 |
| Comparative Tracking Index | CTI | UL746 | PLC 2 |
| High Amp Arc Ignition | HAI | UL746 | PLC 2 |
| Volume Resistivity | ASTMD257 | 1.2E+16 ohms·cm | |
| Dielectric Strength | 3.20mm,inOil | ASTMD149 | 17 KV/mm |
| Hot-wire Ignition | HWI | UL746 | PLC 0 |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC 3 |