ABS J-1200/20 USA TLC
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D-792 | 1.23 g/cm | |
| Shrinkage rate | 3.18mm | ASTM D-955 | 0.30 % |
| 6.35mm | ASTM D-955 | 0.30 % |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D-570 | 0.30 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| bending strength | 23℃，断裂 | ASTM D-790 | 110 MPa |
| Impact strength of cantilever beam gap | 23℃,3.18mm | ASTM D-256 | 80.1 J/m |
| elongation at break | 23℃ | ASTM D-638 | 2.0 % |
| Flexural modulus | 23℃ | ASTM D-790 | 5860 MPa |
| Rockwell hardness | ASTM D-785 | 75 M scale | |
| Tensile modulus | 23℃ | ASTM D-638 | 6210 MPa |
| tensile strength | 23℃，断裂 | ASTM D-638 | 82.7 MPa |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa，未退火，HDT | ASTM D-648 | 98.9 ℃ |
| combustibility | 1.47mm | UL 94 | HB |
| 3.05mm | UL 94 | HB | |
| 6.10mm | UL 94 | HB | |
| RTI Str | 1.47mm | UL 746 | 60.0 ℃ |
| 3.05mm | UL 746 | 60.0 ℃ | |
| 6.10mm | UL 746 | 60.0 ℃ | |
| Heat distortion temperature | 0.45MPa，未退火，HDT | ASTM D-648 | 107 ℃ |
| RTI Imp | 1.47mm | UL 746 | 60.0 ℃ |
| 3.05mm | UL 746 | 60.0 ℃ | |
| 6.10mm | UL 746 | 60.0 ℃ | |
| RTI Elec | 1.47mm | UL 746 | 60.0 ℃ |
| 3.05mm | UL 746 | 60.0 ℃ | |
| 6.10mm | UL 746 | 60.0 ℃ |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.