ABS J-1200/20 USA TLC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | USA TLC/J-1200/20 |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D-570 | 0.30 % |
| Mechanical properties | Test Condition | Test Method | USA TLC/J-1200/20 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23℃,3.18mm | ASTM D-256 | 80.1 J/m |
| tensile strength | 23℃，断裂 | ASTM D-638 | 82.7 MPa |
| Rockwell hardness | ASTM D-785 | 75 M scale | |
| elongation at break | 23℃ | ASTM D-638 | 2.0 % |
| bending strength | 23℃，断裂 | ASTM D-790 | 110 MPa |
| Tensile modulus | 23℃ | ASTM D-638 | 6210 MPa |
| Flexural modulus | 23℃ | ASTM D-790 | 5860 MPa |
| physical property | Test Condition | Test Method | USA TLC/J-1200/20 |
|---|---|---|---|
| Shrinkage rate | 6.35mm | ASTM D-955 | 0.30 % |
| density | ASTM D-792 | 1.23 g/cm | |
| Shrinkage rate | 3.18mm | ASTM D-955 | 0.30 % |
| Thermal performance | Test Condition | Test Method | USA TLC/J-1200/20 |
|---|---|---|---|
| RTI Imp | 3.05mm | UL 746 | 60.0 ℃ |
| RTI Str | 1.47mm | UL 746 | 60.0 ℃ |
| 6.10mm | UL 746 | 60.0 ℃ | |
| combustibility | 6.10mm | UL 94 | HB |
| Heat distortion temperature | 0.45MPa，未退火，HDT | ASTM D-648 | 107 ℃ |
| 1.80MPa，未退火，HDT | ASTM D-648 | 98.9 ℃ | |
| RTI Elec | 3.05mm | UL 746 | 60.0 ℃ |
| RTI Str | 3.05mm | UL 746 | 60.0 ℃ |
| RTI Elec | 1.47mm | UL 746 | 60.0 ℃ |
| combustibility | 1.47mm | UL 94 | HB |
| RTI Elec | 6.10mm | UL 746 | 60.0 ℃ |
| RTI Imp | 1.47mm | UL 746 | 60.0 ℃ |
| 6.10mm | UL 746 | 60.0 ℃ | |
| combustibility | 3.05mm | UL 94 | HB |