برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.03 g/cm3 |
| Shrinkage rate | MD | ASTM D955 | 0.70-0.90 % |
| density | | ASTM D792 | 1.03 g/cm³ |
| Shrinkage rate | MD | ASTM D955 | 0.70to0.90 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 104 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | | ASTM D785 | 104 R 计秤 |
| Fracture tensile strength | 断裂 | ASTM D638 | 49.0 MPa |
| elongation at yield | | ASTM D638 | 50 % |
| Flexural modulus | | ASTM D790 | 2000 MPa |
| bending strength | | ASTM D790 | 57.9 MPa |
| Impact strength of cantilever beam gap | 3.18mm | ASTM D256 | 320 J/m |
| tensile strength | Break | ASTM D638 | 49.0 MPa |
| elongation | Yield | ASTM D638 | 50 % |
| Flexural modulus | | ASTM D790 | 2000 MPa |
| bending strength | | ASTM D790 | 57.9 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 3.18mm | ASTM D256 | 320 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 85.0 ℃ |
| UL flame retardant rating | 1.59mm | UL 94 | HB |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 85.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.