برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | TD:3.20mm | ISO 2577 | 0.31-0.38 % |
| Shrinkage rate | MD:3.20mm | ISO 2577 | 0.29-0.36 % |
| density | | ASTM D792 | 1.10 g/cm³ |
| density | | ISO 1183 | 1.10 g/cm³ |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 13 g/10min |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 13 g/10min |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.29-0.36 % |
| Shrinkage rate | TD：3.20mm | ASTM D955 | 0.31-0.38 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Hardness | | JISK5401 | H |
| Rockwell hardness | R级 | ASTM D785 | 116 |
| Rockwell hardness | R级 | ISO 2039-2 | 116 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ASTM D638 | 2500 Mpa |
| Tensile modulus | | ISO 527-2/50 | 2600 Mpa |
| tensile strength | 屈服 | ASTM D638 | 51.0 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 55.0 Mpa |
| tensile strength | 断裂 | ASTM D638 | 34.0 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 40.0 Mpa |
| elongation | 断裂 | ASTM D638 | 25 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 20 % |
| Flexural modulus | | ASTM D790 | 2600 Mpa |
| Flexural modulus | | ISO 178 | 2700 Mpa |
| bending strength | | ASTM D790 | 74.0 Mpa |
| bending strength | | ISO 178 | 85.0 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 110 J/m |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 98 J/m |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 9.0 kJ/m² |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 98.0 °C |
| Heat distortion temperature | 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 91.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 92.0 °C |
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 78.0 °C |
| vicat | | ISO 306/B50 | 100 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.