PEEK LUVOCOM® 1105-9020/T LEHVOSS Group
0
- ویژگیها:Fillerscarbon fiber reinforced materials
- کاربردها:Applications in the automotive industrybushingsmedicalnursing suppliestextile applicationspumpsaerospace applicationsengineering accessoriesgearsbearings
برگه داده فنی
physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
density | ISO 1183 | 1.62 g/cm³ | |
Shrinkage rate | MD | ISO 294-4 | 0.2 % |
TD | ISO 294-4 | 0.6 % | |
Water absorption rate | (23°C,24hr) | ISO 62 | <=0.1 % |
melt mass-flow rate | 380℃/10.0Kg | ISO 1133 | 15 g/10min |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
tensile strength | 23°C | ISO 527-2 | 155 MPa |
elongation at break | 23°C | ISO 527-2 | 1.6 % |
bending strength | 应变2.1%,23°C | ISO 178 | 215 MPa |
Flexural modulus | 23°C | ISO 178 | 13000 MPa |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 28 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 30 kJ/m² |
Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
Dissipation Factor | 体积电阻 | <=1.0E+5 Ω.cm | |
表面电阻 | <=1.0E+7 Ω.cm |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
Linear coefficient of thermal expansion | 最高使用温度 | 250 °C | |
最高使用温度 | 270 °C | ||
vicat | ISO 306/A50 | 320 °C | |
Heat distortion temperature | 1.80MPa退火,HDT | ISO 75-2/Af | 260 °C |
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.