برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.68 g/cm³ |
| melt mass-flow rate | 275°C/2.16kg | ASTM D1238 | 18to20 g/10min |
| Shrinkage rate | MD | ASTM D955 | 2.5 % |
| Water absorption rate | Equilibrium | ASTM D570 | <0.10 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 90 |
| Shore hardness | 邵氏D | ASTM D2240 | 75 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Limiting Oxygen Index | | ASTM D2863 | 52 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation | 屈服,23°C | ASTM D638 | 5.0 % |
| elongation | 断裂,23°C | ASTM D638 | 250 % |
| Flexural modulus | 23°C | ASTM D790 | 1690 MPa |
| bending strength | 23°C | ASTM D790 | 47.0 MPa |
| coefficient of friction | Itself - Dynamic | ASTM D1894 | 0.20 |
| coefficient of friction | Itself - Static | ASTM D1894 | 0.20 |
| Tensile modulus | 23°C | ASTM D638 | 1660 MPa |
| tensile strength | 屈服,23°C | ASTM D638 | 30.0 MPa |
| tensile strength | 断裂,23°C | ASTM D638 | 54.0 MPa |
| coefficient of friction | 泰伯耐磨性(1000Cycles,500g,CS-17转轮) | ASTM D1894 | 5.00 mg |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | -40°C,3.20mm | ASTM D256 | 210 J/m |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 无断裂 |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| dielectric strength | 23°C,3.20mm | ASTM D149 | 14 kV/mm |
| dielectric constant | 23°C,1MHz | ASTM D150 | 2.57 |
| Volume resistivity | 23°C | ASTM D257 | 5.5E+16 ohms·cm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 65.0 °C |
| brittle temperature | | ASTM D746A | <-76.0 °C |
| Glass Transition Temperature | | DMA | 85.0 °C |
| melting temperature | | ASTM D3418 | 242 °C |
| Crystallization peak temperature | DSC | ASTM D3418 | 222 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 1E-04 cm/cm/°C |
| specific heat | 23°C | ASTM D3418 | 962 J/kg/°C |
| thermal conductivity | 40°C | ASTMC177 | 0.15 W/m/K |
| Crystallization peak temperature | | ASTM D3418 | 40.0 J/g |
| thermal stability | | TGA | 405 °C |
| Fusion temperature | | ASTM D3418 | 42.0 J/g |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 90.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.