Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ECTFE Halar® 513LC SOLVAY BELGIUM
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY BELGIUM/Halar® 513LC |
|---|---|---|---|
| Impact strength of cantilever beam gap | -40°C,3.20mm | ASTM D256 | 210 J/m |
| 23°C,3.20mm | ASTM D256 | 无断裂 |
| hardness | Test Condition | Test Method | SOLVAY BELGIUM/Halar® 513LC |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 75 |
| Rockwell hardness | R级 | ASTM D785 | 90 |
| Mechanical properties | Test Condition | Test Method | SOLVAY BELGIUM/Halar® 513LC |
|---|---|---|---|
| coefficient of friction | 泰伯耐磨性(1000Cycles,500g,CS-17转轮) | ASTM D1894 | 5.00 mg |
| bending strength | 23°C | ASTM D790 | 47.0 MPa |
| tensile strength | 断裂,23°C | ASTM D638 | 54.0 MPa |
| coefficient of friction | 与自身-动态 | ASTM D1894 | 0.20 |
| Tensile modulus | 23°C | ASTM D638 | 1660 MPa |
| Flexural modulus | 23°C | ASTM D790 | 1690 MPa |
| elongation | 屈服,23°C | ASTM D638 | 5.0 % |
| tensile strength | 屈服,23°C | ASTM D638 | 30.0 MPa |
| elongation | 断裂,23°C | ASTM D638 | 250 % |
| coefficient of friction | 与自身-静态 | ASTM D1894 | 0.20 |
| Electrical performance | Test Condition | Test Method | SOLVAY BELGIUM/Halar® 513LC |
|---|---|---|---|
| dielectric constant | 23°C,1MHz | ASTM D150 | 2.57 |
| Volume resistivity | 23°C | ASTM D257 | 5.5E+16 ohms·cm |
| dielectric strength | 23°C,3.20mm | ASTM D149 | 14 kV/mm |
| flammability | Test Condition | Test Method | SOLVAY BELGIUM/Halar® 513LC |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Limiting Oxygen Index | ASTM D2863 | 52 % |
| physical property | Test Condition | Test Method | SOLVAY BELGIUM/Halar® 513LC |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 2.5 % |
| Water absorption rate | 平衡 | ASTM D570 | <0.10 % |
| density | ASTM D792 | 1.68 g/cm³ | |
| melt mass-flow rate | 275°C/2.16kg | ASTM D1238 | 18to20 g/10min |
| Thermal performance | Test Condition | Test Method | SOLVAY BELGIUM/Halar® 513LC |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 65.0 °C |
| thermal conductivity | 40°C | ASTMC177 | 0.15 W/m/K |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 90.0 °C |
| Crystallization peak temperature | DSC | ASTM D3418 | 222 °C |
| ASTM D3418 | 40.0 J/g | ||
| Fusion temperature | ASTM D3418 | 42.0 J/g | |
| thermal stability | TGA | 405 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 1E-04 cm/cm/°C |
| Glass Transition Temperature | DMA | 85.0 °C | |
| melting temperature | ASTM D3418 | 242 °C | |
| brittle temperature | ASTM D746A | <-76.0 °C | |
| specific heat | 23°C | ASTM D3418 | 962 J/kg/°C |