| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.37 g/cm³ |
| Shrinkage rate | MD | ASTM D955 | 1.4 % |
| Shrinkage rate | TD | ASTM D955 | 1.4 % |
| Water absorption rate | Saturation | ASTM D570 | 0.50 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| Burning wire flammability index | 1.0到2.0mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.0到2.0mm | IEC 60695-2-13 | 775 °C |
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ASTM D638 | 4000 MPa |
| tensile strength | Yield | ASTM D638 | 70.0 MPa |
| elongation | Break | ASTM D638 | 2.0 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | | ISO 180/A | 3.0 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 30 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648A | 120 °C |
| vicat | | ASTM D15252 | 210 °C |
| RTI Elec | | UL 746 | 140 °C |
| RTI Imp | | UL 746 | 140 °C |
| RTI | | UL 746 | 140 °C |