MMW-HDPE TOTAL Polyethylene HDPE HL 535
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 0.955 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.35 g/10min |
| 190°C/21.6kg | ASTM D1238 | 30 g/10min |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| film thickness | 25 µm | ||
| Secant modulus | 25µm,BlownFilm | ASTM D882A | 917 MPa |
| 25µm,BlownFilm | ASTM D882A | 1280 MPa | |
| tensile strength | Yield,25µm,BlownFilm | ASTM D882A | 27.6 MPa |
| Yield,25µm,BlownFilm | ASTM D882A | 29.6 MPa | |
| Tensile strain | Break,25µm,BlownFilm，MD | ASTM D882A | 500 % |
| Break,25µm,BlownFilm | ASTM D882A | 25 % | |
| Dart impact | 25µm,吹塑薄膜 | ASTM D1709A | <50 g |
| Elmendorf tear strength | 25µm,BlownFilm，MD | ASTM D1922 | 8.0 g |
| 25µm,BlownFilm，TD | ASTM D1922 | 1100 g | |
| Water Vapor Transmission Rate | 38°C,25µm,BlownFilm | ASTMF1249 | 11 g/m²/24hr |
| tensile strength | Break,25µm,BlownFilm | ASTM D882A | 43.4 MPa |
| Break,25µm,BlownFilm | ASTM D882A | 29.6 MPa |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melting temperature | ASTM D3417 | 132 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.