برگه داده فنی
physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Shrinkage rate | 横向流量 | ISO 294-4 | 0.80 % |
Shrinkage rate | 流量 | ISO 294-4 | 0.30 % |
Water absorption rate | 24 hr, 23°C | ISO 62 | 0.83 % |
Water absorption rate | 饱和, 23°C, 2.00 mm | ISO 62 | 4.5 % |
Water absorption rate | 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.5 % |
flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
burning rate | 1.00 mm | ISO 3795 | 23 mm/min |
UL flame retardant rating | | UL 94 | HB |
UL flame retardant rating | | UL 94 | HB |
Limiting Oxygen Index | | ISO 4589-2 | 23 % |
FMVSS combustion rate | | FMVSS 302 | SE/B |
雾化 - G-value (condensate) | | ISO 6452 | 8.0E-4 g |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Tensile modulus | | ISO 527-2 | 8700 Mpa |
tensile strength | 断裂 | ISO 527-2 | 142 Mpa |
Tensile strain | 断裂 | ISO 527-2 | 4.0 % |
Flexural modulus | | ISO 178 | 7400 Mpa |
Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 80 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 91 kJ/m² |
Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 80 kJ/m² |
Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 74 kJ/m² |
Filling analysis | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Melt density | | | 1.12 g/cm³ |
Ejection Temperature | | | 210 °C |
Specific Heat Capacity of Melt | | | 2200 J/kg/°C |
Thermal Conductivity of Melt | | | 0.22 W/m/K |
Emission of Organic Compounds | | VDA 277 | 25.0 µgC/g |
Odor | | VDA 270 | 3.00 |
Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
drying temperature | | | 80 °C |
Drying time - hot air dryer | | | 2.0 to 4.0 hr |
Suggested maximum moisture content | | | 0.20 % |
Processing (melt) temperature | | | 285 to 305 °C |
Melt Temperature, Optimum | | | 295 °C |
Temperature | | | 50 to 100 °C |
Mold Temperature, Optimum | | | 80 °C |
pressure holding | | | 50.0 to 100 Mpa |
pressure holding | Drying Recommended | | yes |
Hold Pressure Time | | | 3.00 s/mm |
Maximum Screw Tangential Speed | | | 12 m/min |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Heat distortion temperature | 0.45 MPa, 未退火,HDT | ISO 75-2/B | 262 °C |
Heat distortion temperature | 1.8 MPa, 未退火,HDT | ISO 75-2/A | 247 °C |
melting temperature | | ISO 11357-3 | 262 °C |
Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.5E-5 cm/cm/°C |
Linear coefficient of thermal expansion | 横向 | ISO 11359-2 | 1.2E-4 cm/cm/°C |
Effective thermal diffusivity coefficient | | | 8.50E-8 m²/s |
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.