| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.07 g/cm³ |
| melt mass-flow rate | 220℃/10.0Kg | ISO 1133 | 9 g/10min |
| melt mass-flow rate | 线性收缩率 | ISO 294-4 | 0.5-0.7 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ball-indentation hardness | | ISO 2039-1 | 105 Mpa |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Flexural modulus | 23°C | ISO 178 | 2300 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 60 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 12 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 220 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 160 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 30 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 12 kJ/m² |
| tensile strength | 屈服，23°C | ISO 527-2 | 49 Mpa |
| elongation at break | 屈服，23°C | ISO 527-2 | 3 % |
| elongation at break | 23°C | ISO 527-2 | >=15 % |
| Tensile modulus | 23°C | ISO 527-2 | 2400 Mpa |
| bending strength | 23°C | ISO 178 | 77 Mpa |
| Other performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melting temperature | | ISO 294 | 240 °C |
| injection speed | | ISO 294 | 240 mm/sec |
| burning rate | | ISO 3795 | 45 mm/min |
| Flame retardant performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| GWIT | 2.00mm | IEC 60695-2-12 | 700 °C |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | IEC 60093 | 1E+14 Ω.cm |
| Surface Resistivity | | IEC 60093 | 1E+16 Ω.cm |
| dielectric strength | 1.00mm | IEC 60243-1 | 38 KV/mm |
| dielectric constant | | IEC 60250 | 3 1MHz |
| dielectric constant | | IEC 60250 | 3.1 100HZ |
| Dissipation Factor | | IEC 60250 | 0.05 |
| Dissipation Factor | | IEC 60250 | 0.09 |
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 600 V |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 106 °C |
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 99 °C |
| vicat | 5.10kg | ISO 306/A50 | 105 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.