Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS H801 INEOS STYRO THAILAND
Novodur®
Home appliance components、Phone case、Seat、Automotive interior parts、Application in the automo、Automotive interior equip
UV resistance、High temperature resistan、Weather resistance、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | INEOS STYRO THAILAND/H801 |
|---|---|---|---|
| Melting temperature | ISO294 | 240 °C | |
| burning rate | ISO3795 | 45 mm/min | |
| injection speed | ISO294 | 240 mm/sec |
| hardness | Test Condition | Test Method | INEOS STYRO THAILAND/H801 |
|---|---|---|---|
| Ball Indentation Hardness | ISO2039-1 | 105 Mpa |
| Mechanical properties | Test Condition | Test Method | INEOS STYRO THAILAND/H801 |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 12 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 220 kJ/m² |
| -30°C | ISO179/1eU | 160 kJ/m² | |
| Flexural modulus | 23°C | ISO178 | 2300 Mpa |
| Tensile modulus | 23°C | ISO527-2 | 2400 Mpa |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 30 kJ/m² |
| tensile strength | 屈服，23°C | ISO527-2 | 49 Mpa |
| elongation at break | 23°C | ISO527-2 | >=15 % |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 12 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 60 kJ/m² |
| elongation at break | 屈服，23°C | ISO527-2 | 3 % |
| bending strength | 23°C | ISO178 | 77 Mpa |
| Electrical performance | Test Condition | Test Method | INEOS STYRO THAILAND/H801 |
|---|---|---|---|
| dielectric constant | IEC60250 | 3 1MHz | |
| Volume Resistivity | IEC60093 | 1E+14 Ω.cm | |
| Dissipation Factor | IEC60250 | 0.09 | |
| dielectric constant | IEC60250 | 3.1 100HZ | |
| Surface Resistivity | IEC60093 | 1E+16 Ω.cm | |
| Dissipation Factor | 相对漏电起痕指数 | IEC60112 | 600 V |
| Dielectric Strength | 1.00mm | IEC60243-1 | 38 KV/mm |
| Flame retardant performance | Test Condition | Test Method | INEOS STYRO THAILAND/H801 |
|---|---|---|---|
| GWIT | 2.00mm | IEC60695-2-12 | 700 °C |
| physical property | Test Condition | Test Method | INEOS STYRO THAILAND/H801 |
|---|---|---|---|
| Melt Mass-Flow Rate | 220℃/10.0Kg | ISO1133 | 9 g/10min |
| density | ISO1183 | 1.07 g/cm³ | |
| Melt Mass-Flow Rate | 线性收缩率 | ISO294-4 | 0.5-0.7 % |
| Thermal performance | Test Condition | Test Method | INEOS STYRO THAILAND/H801 |
|---|---|---|---|
| Heat Deflection Temperature | 1.80MPa退火 | ISO75-2/Af | 99 °C |
| 0.45MPa未退火 | ISO75-2/Bf | 106 °C | |
| Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 8E-05 cm/cm/°C |
| vicat | 5.10kg | ISO306/A50 | 105 °C |