HDPE PRE-ELEC® TP 11270 Premix Oy

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	23°C	ASTM D256	13 kJ/m²
Impact strength of simply supported beam without notch	-20°C	ISO 179	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	无断裂
Impact strength of cantilever beam gap	-20°C,4.00mm	ASTM D256	4.20 kJ/m²
	Impact strength of cantilever beam gap	23°C,4.00mm	ASTM D256	12.6 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-20°C	ISO 180	5.0 kJ/m²
Charpy Notched Impact Strength	-20°C	ISO 179	4.0 kJ/m²
	Charpy Notched Impact Strength	-20°C	ASTM D256	4.2 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	12 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180	13 kJ/m²
Suspended wall beam without notch impact strength	-20°C,4.00mm	ASTM D256	无断裂
	Suspended wall beam without notch impact strength	23°C,4.00mm	ASTM D256	无断裂
		Suspended wall beam without notch impact strength	-20°C	ISO 180	无断裂
		Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180	无断裂

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Flow:Yield	ASTM D638	24.8 MPa
	tensile strength	横向Flow:Yield	ASTM D638	24.8 MPa
		tensile strength	Flow:Yield	ISO 527-2	25.0 MPa
			tensile strength	横向Flow:Yield	ISO 527-2	25.0 MPa
				tensile strength	Flow	ASTM D638	46.2 MPa
					tensile strength	横向Flow	ASTM D638	26.2 MPa
						tensile strength	4.00mm2	ISO 527-2	46.0 MPa
						tensile strength	tensile strength	4.00mm3	ISO 527-2	27.0 MPa
elongation	Flow:Yield	ASTMD638	26 %
	elongation	横向Flow:Yield	ASTMD638	8.0 %
		elongation	Flow:Break	ASTM D638	>600 %
			elongation	横向Flow:Break	ASTM D638	>600 %
				elongation	Break,4.00mm2	ISO 527-2	>600 %
				elongation	elongation	Break,0.400mm3	ISO 527-2	>600 %
Bending modulus	4.00mm	ASTMD790	1200 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Vicat softening temperature	--	ASTMD15256	127 °C
	Vicat softening temperature	--	ISO 306/B50	87.0 °C
	Vicat softening temperature	Vicat softening temperature	--	ASTM D15255	60.0 °C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648B	82.2 °C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	76.0 °C
		Hot deformation temperature	1.8MPa,Unannealed	ASTM D648A	47.8 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	45.0 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	MD	ASTM D955	2.5to3.5 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	2.5to3.5 %
density	--	ASTM D792	1.05 g/cm³
density	density	--	ISO 1183	1.03 g/cm³
melt mass-flow rate	190°C/21.6kg	ASTMD1238	15 g/10min

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface resistivity		ESDSTM11.11,IEC61340-2-3	<1.0E+5 ohms
Volume resistivity		Internal Method	<1.0E+4 ohms·cm

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Shore hardness	ShoreA	ASTMD2240	97
Shore hardness	Shore hardness	ShoreD	ASTMD2240	70