HDPE PRE-ELEC® TP 11270 Premix Oy
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodPremix Oy/PRE-ELEC® TP 11270
Charpy Notched Impact Strength-20°CASTM D2564.2 kJ/m²
Impact strength of cantilever beam gap23°CISO 18013 kJ/m²
Charpy Notched Impact Strength23°CASTM D25613 kJ/m²
Impact strength of cantilever beam gap-20°CISO 1805.0 kJ/m²
Suspended wall beam without notch impact strength-20°C,4.00mmASTM D256无断裂
Impact strength of simply supported beam without notch-20°CISO 179无断裂
Charpy Notched Impact Strength23°CISO 17912 kJ/m²
Impact strength of cantilever beam gap23°C,4.00mmASTM D25612.6 kJ/m²
-20°C,4.00mmASTM D2564.20 kJ/m²
Suspended wall beam without notch impact strength-20°CISO 180无断裂
Impact strength of simply supported beam without notch23°CISO 179无断裂
Charpy Notched Impact Strength-20°CISO 1794.0 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180无断裂
23°C,4.00mmASTM D256无断裂
hardnessTest ConditionTest MethodPremix Oy/PRE-ELEC® TP 11270
Shore hardness邵氏DASTMD224070
邵氏AASTMD224097
Mechanical propertiesTest ConditionTest MethodPremix Oy/PRE-ELEC® TP 11270
tensile strength 4.00mm2ISO 527-246.0 MPa
横向流量ASTM D63826.2 MPa
elongation横向流量:屈服ASTMD6388.0 %
tensile strength 流量:屈服ISO 527-225.0 MPa
横向流量:屈服ISO 527-225.0 MPa
4.00mm3ISO 527-227.0 MPa
Flexural modulus4.00mmASTMD7901200 MPa
elongation横向流量:断裂ASTM D638>600 %
流量:屈服ASTMD63826 %
流量:断裂ASTM D638>600 %
tensile strength 横向流量:屈服ASTM D63824.8 MPa
流量:屈服ASTM D63824.8 MPa
elongation断裂,4.00mm2ISO 527-2>600 %
断裂,0.400mm3ISO 527-2>600 %
tensile strength 流量ASTM D63846.2 MPa
Electrical performanceTest ConditionTest MethodPremix Oy/PRE-ELEC® TP 11270
Surface ResistivityESDSTM11.11,IEC61340-2-3<1.0E+5 ohms
Volume resistivity内部方法<1.0E+4 ohms·cm
physical property Test ConditionTest MethodPremix Oy/PRE-ELEC® TP 11270
Shrinkage rateMDASTM D9552.5to3.5 %
melt mass-flow rate190°C/21.6kgASTMD123815 g/10min
Shrinkage rateMDISO 294-42.5to3.5 %
density--ASTM D7921.05 g/cm³
--ISO 11831.03 g/cm³
Thermal performanceTest ConditionTest MethodPremix Oy/PRE-ELEC® TP 11270
Heat distortion temperature1.8MPa,未退火，HDTASTM D648A47.8 °C
1.8MPa,未退火，HDTISO 75-2/Af45.0 °C
0.45MPa,未退火，HDTASTM D648B82.2 °C
vicat--ASTM D1525560.0 °C
--ISO 306/B5087.0 °C
--ASTMD15256127 °C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/Bf76.0 °C