برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | | ISO 2577 | 0.40to0.60 % |
| density | | ASTM D792 | 1.17 g/cm³ |
| density | 23°C | ISO 1183 | 1.17 g/cm³ |
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 20 g/10min |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 21.0 cm³/10min |
| spiral flow length | | 内部方法 | 45.0 cm |
| Shrinkage rate | MD | ASTM D955 | 0.40to0.60 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R计秤,23°C | ASTM D785 | 113 |
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 113 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| UL flame retardant rating | 2.1mm | UL 94 | 5VB |
| UL flame retardant rating | 3.0mm | UL 94 | 5VA |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | Yield,23°C | ASTM D638 | 49.0 MPa |
| tensile strength | Yield | ISO 527-2/50 | 55.0 MPa |
| tensile strength | Break | ISO 527-2/50 | 45.0 MPa |
| Tensile strain | Break,23°C | ASTM D638 | 100 % |
| Tensile strain | Break | ISO 527-2/50 | 110 % |
| Flexural modulus | 23°C | ASTM D790 | 245 MPa |
| Flexural modulus | | ISO 178 | 2500 MPa |
| bending strength | 23°C | ASTM D790 | 78.5 MPa |
| bending strength | | ISO 178 | 80.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179 | 15 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 45 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 590 J/m |
| Impact strength of cantilever beam gap | -30°C | ISO 180 | 15 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 45 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 2.9E+17 ohms |
| Volume resistivity | | IEC 60093 | 3.9E+19 ohms·cm |
| dielectric constant | 1MHz | IEC 60250 | 3.10 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| vicat | -- | ASTM D152510 | 94.0 °C |
| vicat | -- | ASTM D152511 | 85.0 °C |
| vicat | -- | ISO 306/A50 | 94.0 °C |
| vicat | -- | ISO 306/B50 | 85.0 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 78.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 87.0 °C |
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 73.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.