PC WONDERLOY® PC-510 CHI MEI CORPORATION
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CHI MEI CORPORATION/WONDERLOY® PC-510 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 45 kJ/m² |
| -30°C | ISO 179 | 15 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 45 kJ/m² |
| -30°C | ISO 180 | 15 kJ/m² | |
| 23°C,3.18mm | ASTM D256 | 590 J/m |
| hardness | Test Condition | Test Method | CHI MEI CORPORATION/WONDERLOY® PC-510 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTM D785 | 113 |
| R计秤,23°C | ISO 2039-2 | 113 |
| Mechanical properties | Test Condition | Test Method | CHI MEI CORPORATION/WONDERLOY® PC-510 |
|---|---|---|---|
| tensile strength | Yield,23°C | ASTM D638 | 49.0 MPa |
| Tensile strain | Break,23°C | ASTM D638 | 100 % |
| bending strength | 23°C | ASTM D790 | 78.5 MPa |
| Flexural modulus | 23°C | ASTM D790 | 245 MPa |
| ISO 178 | 2500 MPa | ||
| Tensile strain | 断裂 | ISO 527-2/50 | 110 % |
| tensile strength | 屈服 | ISO 527-2/50 | 55.0 MPa |
| bending strength | ISO 178 | 80.0 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 45.0 MPa |
| Electrical performance | Test Condition | Test Method | CHI MEI CORPORATION/WONDERLOY® PC-510 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 3.9E+19 ohms·cm | |
| dielectric constant | 1MHz | IEC 60250 | 3.10 |
| Surface Resistivity | IEC 60093 | 2.9E+17 ohms |
| flammability | Test Condition | Test Method | CHI MEI CORPORATION/WONDERLOY® PC-510 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | 5VA |
| 2.1mm | UL 94 | 5VB | |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | CHI MEI CORPORATION/WONDERLOY® PC-510 |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | 0.40to0.60 % | |
| spiral flow length | 内部方法 | 45.0 cm | |
| density | 23°C | ISO 1183 | 1.17 g/cm³ |
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 20 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.40to0.60 % |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 21.0 cm³/10min |
| density | ASTM D792 | 1.17 g/cm³ |
| Thermal performance | Test Condition | Test Method | CHI MEI CORPORATION/WONDERLOY® PC-510 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 73.0 °C |
| vicat | -- | ASTM D152511 | 85.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 87.0 °C |
| vicat | -- | ASTM D152510 | 94.0 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| vicat | -- | ISO 306/A50 | 94.0 °C |
| -- | ISO 306/B50 | 85.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 78.0 °C |