PC CY6110 resin
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.60 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.60 % |
| 平衡,23°C,50%RH | ISO 62 | 0.20 % | |
| density | ISO 1183 | 1.18 g/cm³ | |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 23.0 cm³/10min |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| 2.5mm | UL 94 | 5VB | |
| Burning wire flammability index | 0.75mm10 | IEC 60695-2-12 | 960 °C |
| 1.0mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 0.75mm10 | IEC 60695-2-13 | 775 °C |
| 1.0mm | IEC 60695-2-13 | 825 °C | |
| 1.5mm10 | IEC 60695-2-13 | 775 °C | |
| 2.0mm | IEC 60695-2-13 | 825 °C | |
| 3.0mm10 | IEC 60695-2-13 | 775 °C | |
| 3.0mm | IEC 60695-2-13 | 825 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Limiting Oxygen Index | ISO 4589-2 | 31 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | --3 | ASTM D638 | 2760 MPa |
| -- | ISO 527-2/1 | 2750 MPa | |
| tensile strength | 屈服4 | ASTM D638 | 63.9 MPa |
| Yield | ISO 527-2/50 | 63.1 MPa | |
| 断裂4 | ASTM D638 | 47.5 MPa | |
| elongation | Yield | ISO 527-2/50 | 4.0 % |
| 断裂4 | ASTM D638 | 65 % | |
| Break | ISO 527-2/50 | 35 % | |
| Flexural modulus | ISO 178 | 2440 MPa | |
| bending strength | ISO 178 | 94.5 MPa | |
| tensile strength | Break | ISO 527-2/50 | 46.4 MPa |
| elongation | 屈服4 | ASTM D638 | 4.1 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂无断裂 |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 100 J/m |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 1010 kJ/m² |
| 23°C | ISO 179/1eA | 33 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂无断裂 |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 480 J/m |
| -30°C8 | ISO 180/1A | 12 kJ/m² | |
| 23°C8 | ISO 180/1A | 25 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂无断裂 |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| relative permittivity | 60Hz | IEC 60250 | 2.90 |
| 1MHz | IEC 60250 | 2.90 | |
| Dissipation Factor | 50Hz | IEC 60250 | 2E-03 |
| 60Hz | IEC 60250 | 2E-03 | |
| 1MHz | IEC 60250 | 7E-03 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 46 kV/mm |
| 1.60mm,在油中 | IEC 60243-1 | 31 kV/mm | |
| relative permittivity | 50Hz | IEC 60250 | 2.90 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 106 °C |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | MD:-40到40°C | ISO 11359-2 | 8E-06 cm/cm/°C |
| TD:-40到40°C | ISO 11359-2 | 8E-06 cm/cm/°C | |
| RTI Elec | UL 746 | 85.0 °C | |
| RTI Imp | UL 746 | 85.0 °C | |
| RTI | UL 746 | 85.0 °C | |
| Heat distortion temperature | 0.45MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Bf | 98.6 °C |
| 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 88.1 °C | |
| vicat | -- | ISO 306/B50 | 105 °C |