PC CY6110 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC/CY6110 resin
Charpy Notched Impact Strength23°CISO 179/1eA33 kJ/m²
Impact strength of cantilever beam gap-30°C8ISO 180/1A12 kJ/m²
-30°CASTM D256100 J/m
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Impact strength of cantilever beam gap23°CASTM D256480 J/m
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂无断裂
Charpy Notched Impact Strength-30°CISO 179/1eA1010 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂无断裂
Impact strength of cantilever beam gap23°C8ISO 180/1A25 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂无断裂
Electrical performanceTest ConditionTest MethodSABIC/CY6110 resin
relative permittivity60HzIEC 602502.90
50HzIEC 602502.90
Volume resistivityIEC 60093>1.0E+15 ohms·cm
dielectric strength1.60mm,在油中IEC 60243-131 kV/mm
Hot wire ignition (HWI)HWIUL 746PLC 3
relative permittivity1MHzIEC 602502.90
Surface ResistivityIEC 60093>1.0E+15 ohms
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 2
Dissipation Factor50HzIEC 602502E-03
60HzIEC 602502E-03
1MHzIEC 602507E-03
dielectric strength0.800mm,在油中IEC 60243-146 kV/mm
Mechanical propertiesTest ConditionTest MethodSABIC/CY6110 resin
elongation断裂4ASTM D63865 %
tensile strength 屈服4ASTM D63863.9 MPa
elongation屈服ISO 527-2/504.0 %
断裂ISO 527-2/5035 %
屈服4ASTM D6384.1 %
Tensile modulus--ISO 527-2/12750 MPa
Flexural modulusISO 1782440 MPa
Tensile modulus--3ASTM D6382760 MPa
tensile strength 断裂4ASTM D63847.5 MPa
屈服ISO 527-2/5063.1 MPa
bending strengthISO 17894.5 MPa
tensile strength 断裂ISO 527-2/5046.4 MPa
flammabilityTest ConditionTest MethodSABIC/CY6110 resin
Hot filament ignition temperature0.75mm10IEC 60695-2-13775 °C
UL flame retardant rating2.5mmUL 945VB
Hot filament ignition temperature2.0mmIEC 60695-2-13825 °C
3.0mmIEC 60695-2-13825 °C
Burning wire flammability index0.75mm10IEC 60695-2-12960 °C
Hot filament ignition temperature1.0mmIEC 60695-2-13825 °C
1.5mm10IEC 60695-2-13775 °C
Burning wire flammability index1.0mmIEC 60695-2-12960 °C
UL flame retardant rating1.5mmUL 94V-0
Limiting Oxygen IndexISO 4589-231 %
Hot filament ignition temperature3.0mm10IEC 60695-2-13775 °C
physical property Test ConditionTest MethodSABIC/CY6110 resin
Shrinkage rateMD：3.20mm内部方法0.40to0.60 %
Water absorption rate平衡,23°C,50%RHISO 620.20 %
Melt volume flow rate260°C/2.16kgISO 113323.0 cm³/10min
Water absorption rate饱和,23°CISO 620.60 %
densityISO 11831.18 g/cm³
Thermal performanceTest ConditionTest MethodSABIC/CY6110 resin
vicat--ISO 306/B120106 °C
Heat distortion temperature0.45MPa,未退火,64.0mm跨距，HDTISO 75-2/Bf98.6 °C
ball-indentation hardness75°CIEC 60695-10-2通过
Linear coefficient of thermal expansionMD:-40到40°CISO 11359-28E-06 cm/cm/°C
vicat--ISO 306/B50105 °C
RTI ImpUL 74685.0 °C
Heat distortion temperature1.8MPa,未退火,64.0mm跨距，HDTISO 75-2/Af88.1 °C
RTIUL 74685.0 °C
Linear coefficient of thermal expansionTD:-40到40°CISO 11359-28E-06 cm/cm/°C
RTI ElecUL 74685.0 °C