برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | -- | ASTM D792 | 1.17 g/cm³ |
| density | -- | ISO 1183/B | 1.18 g/cm³ |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 11 g/10min |
| melt mass-flow rate | 240°C/5.0kg | ASTM D1238 | 20 g/10min |
| melt mass-flow rate | 260°C/2.16kg | ISO 1133 | 13 g/10min |
| Shrinkage rate | MD | ISO 294-4 | 0.40to0.60 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R级,3.20mm,注塑 | ASTM D785 | 120 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 2.5mm | UL 94 | 5VA |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 925 °C |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 925 °C |
| Burning wire flammability index | 2.5mm | IEC 60695-2-12 | 925 °C |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 950 °C |
| Limiting Oxygen Index | | ASTM D2863 | 28 % |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| UL flame retardant rating | 2.0mm | UL 94 | 5VB |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 480 J/m |
| Impact strength of cantilever beam gap | -30°C,注塑 | ISO 180/A | 14 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,注塑 | ISO 180/A | 50 kJ/m² |
| Charpy Notched Impact Strength | -30°C,注塑 | ISO 179/1eA | 15 kJ/m² |
| Charpy Notched Impact Strength | 23°C,注塑 | ISO 179/1eA | 40 kJ/m² |
| Impact strength of cantilever beam gap | -22°C | ASTM D256 | 440 J/m |
| Impact strength of cantilever beam gap | -18°C | ASTM D256 | 200 J/m |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation | 屈服,4.00mm,注塑 | ISO 527-2/50 | 3.8 % |
| elongation | Break | ASTM D638 | 65 % |
| elongation | 断裂,4.00mm,注塑 | ISO 527-2/50 | 43 % |
| Flexural modulus | | ASTM D790 | 2690 MPa |
| bending strength | Yield | ASTM D790 | 96.5 MPa |
| Tensile modulus | -- | ASTM D638 | 2620 MPa |
| Tensile modulus | 4.00mm,注塑 | ISO 527-2/1 | 2560 MPa |
| tensile strength | Yield | ASTM D638 | 60.0 MPa |
| tensile strength | 屈服,4.00mm,注塑 | ISO 527-2/50 | 55.0 MPa |
| tensile strength | Break | ASTM D638 | 48.3 MPa |
| tensile strength | 断裂,3.20mm,注塑 | ISO 527-2/50 | 45.0 MPa |
| elongation | Yield | ASTM D638 | 3.8 % |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 18 kV/mm |
| relative permittivity | 100Hz | IEC 60250 | 2.86 |
| relative permittivity | 1MHz | IEC 60250 | 2.80 |
| Dissipation Factor | 100Hz | IEC 60250 | 4E-03 |
| Dissipation Factor | 1MHz | IEC 60250 | 7E-03 |
| Surface Resistivity | | IEC 60093 | 5.2E+15 ohms |
| Volume resistivity | | IEC 60093 | 1E+18 ohms·cm |
| dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 26 kV/mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 90.6 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 88.0 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 79.4 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 77.0 °C |
| vicat | -- | ASTMD15253 | 104 °C |
| vicat | -- | ISO 306/B50 | 94.0 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTM D696 | 6.8E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTM D696 | 6.8E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.
مقایسه