Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PC/ABS 7710 NA Trinseo
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Trinseo/PC/ABS 7710 NA |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 480 J/m |
| -18°C | ASTM D256 | 200 J/m | |
| -30°C,注塑 | ISO 180/A | 14 kJ/m² | |
| Charpy Notched Impact Strength | 23°C,注塑 | ISO 179/1eA | 40 kJ/m² |
| Impact strength of cantilever beam gap | -22°C | ASTM D256 | 440 J/m |
| 23°C,注塑 | ISO 180/A | 50 kJ/m² | |
| Charpy Notched Impact Strength | -30°C,注塑 | ISO 179/1eA | 15 kJ/m² |
| hardness | Test Condition | Test Method | Trinseo/PC/ABS 7710 NA |
|---|---|---|---|
| Rockwell hardness | R级,3.20mm,注塑 | ASTM D785 | 120 |
| Electrical performance | Test Condition | Test Method | Trinseo/PC/ABS 7710 NA |
|---|---|---|---|
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 18 kV/mm |
| Volume resistivity | IEC 60093 | 1E+18 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 2.86 |
| Dissipation Factor | 100Hz | IEC 60250 | 4E-03 |
| dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 26 kV/mm |
| relative permittivity | 1MHz | IEC 60250 | 2.80 |
| Surface Resistivity | IEC 60093 | 5.2E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 7E-03 |
| Mechanical properties | Test Condition | Test Method | Trinseo/PC/ABS 7710 NA |
|---|---|---|---|
| elongation | 屈服,4.00mm,注塑 | ISO 527-2/50 | 3.8 % |
| 断裂 | ASTM D638 | 65 % | |
| 屈服 | ASTM D638 | 3.8 % | |
| bending strength | 屈服 | ASTM D790 | 96.5 MPa |
| elongation | 断裂,4.00mm,注塑 | ISO 527-2/50 | 43 % |
| Flexural modulus | ASTM D790 | 2690 MPa | |
| tensile strength | 断裂 | ASTM D638 | 48.3 MPa |
| Tensile modulus | -- | ASTM D638 | 2620 MPa |
| tensile strength | 屈服 | ASTM D638 | 60.0 MPa |
| Tensile modulus | 4.00mm,注塑 | ISO 527-2/1 | 2560 MPa |
| tensile strength | 屈服,4.00mm,注塑 | ISO 527-2/50 | 55.0 MPa |
| 断裂,3.20mm,注塑 | ISO 527-2/50 | 45.0 MPa |
| flammability | Test Condition | Test Method | Trinseo/PC/ABS 7710 NA |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 950 °C |
| UL flame retardant rating | 2.5mm | UL 94 | 5VA |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 925 °C |
| UL flame retardant rating | 2.0mm | UL 94 | 5VB |
| Burning wire flammability index | 2.5mm | IEC 60695-2-12 | 925 °C |
| 2.0mm | IEC 60695-2-12 | 925 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Limiting Oxygen Index | ASTM D2863 | 28 % |
| physical property | Test Condition | Test Method | Trinseo/PC/ABS 7710 NA |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294-4 | 0.40to0.60 % |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 11 g/10min |
| density | -- | ASTM D792 | 1.17 g/cm³ |
| -- | ISO 1183/B | 1.18 g/cm³ | |
| melt mass-flow rate | 240°C/5.0kg | ASTM D1238 | 20 g/10min |
| 260°C/2.16kg | ISO 1133 | 13 g/10min |
| Thermal performance | Test Condition | Test Method | Trinseo/PC/ABS 7710 NA |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 79.4 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTM D696 | 6.8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 90.6 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 88.0 °C | |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTM D696 | 6.8E-05 cm/cm/°C |
| vicat | -- | ASTMD15253 | 104 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 77.0 °C |
| vicat | -- | ISO 306/B50 | 94.0 °C |