PAEK AV-722 SOLVAY BELGIUM

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.32 g/cm³
melt mass-flow rate	400°C/2.16kg	ASTM D1238	1.0 g/10min
Shrinkage rate	MD:3.18mm	ASTM D955	0.80to1.0 %
Shrinkage rate	Shrinkage rate	TD:3.18mm	ASTM D955	1.2to1.4 %
Water absorption rate	24hr	ASTM D570	0.10 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	M-Scale	ASTM D785	95

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
Limiting Oxygen Index		ASTM D2863	40 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
compressive strength		ASTM D695	112 MPa
shear strength		ASTM D732	79.0 MPa
Tensile modulus	--3	ASTM D638	3700 MPa
Tensile modulus	Tensile modulus	--	ISO 527-2/1A/1	3900 MPa
tensile strength	Yield	ISO 527-2/1A/50	91.0 MPa
tensile strength	tensile strength	--3	ASTM D638	89.0 MPa
Poisson's ratio		ASTME132	0.43
elongation	屈服3	ASTM D638	5.0 %
	elongation	Yield	ISO 527-2/1A/50	4.5 %
		elongation	断裂3	ASTM D638	25 %
		elongation	elongation	Break	ISO 527-2/1A/50	25 %
Flexural modulus	--	ASTM D790	3700 MPa
Flexural modulus	Flexural modulus	--	ISO 178	3800 MPa
bending strength	--	ASTM D790	141 MPa
bending strength	bending strength	--	ISO 178	138 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	--	ASTM D256	80 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	--	ISO 180	7.0 kJ/m²
Suspended wall beam without notch impact strength		ASTMD4812	无断裂

Filling analysis	شرایط آزمون	روش آزمون	نتیجه آزمون
melt viscosity	400°C,1000sec^-1		450 Pa·s

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
dielectric strength	3.00mm	ASTM D149	19 kV/mm
dielectric constant	60Hz	ASTM D150	3.12
dielectric constant	dielectric constant	1MHz	ASTM D150	3.06
Dissipation Factor	60Hz	ASTM D150	1E-03
Dissipation Factor	Dissipation Factor	1MHz	ASTM D150	4E-03
Surface Resistivity		ASTM D257	>1.9E+17 ohms
Volume resistivity		ASTM D257	3.1E+17 ohms·cm
dielectric strength	0.0500mm,非晶膜	ASTM D149	170 kV/mm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Glass Transition Temperature		ASTM D3418	150 °C
melting temperature		ASTM D3418	340 °C
Linear coefficient of thermal expansion	MD：-50到50°C	ASTME831	4.5E-05 cm/cm/°C
specific heat	50°C	DSC	1410 J/kg/°C
specific heat	specific heat	200°C	DSC	1970 J/kg/°C
Heat distortion temperature	1.8MPa,退火,3.20mm，HDT	ASTM D648	161 °C
thermal conductivity		ASTME1530	0.22 W/m/K