برگه داده فنی
Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
density | | ASTM D-792 | 0.91 g/cm |
melt mass-flow rate | 230℃,2.16Kg | ASTM D-1238 | 0.4 g/10min |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Impact strength of cantilever beam gap | 23℃ | ASTM D-256 | 无破损 kg.cm/cm |
Flexural modulus | | ASTM D-790 | 11500 kg/cm |
Impact strength of cantilever beam gap | -20℃ | ASTM D-256 | 6 kg.cm/cm |
elongation at break | | ASTM D-638 | 500 % |
tensile strength | 屈服点 | ASTM D-638 | 270 kg/cm |
tensile strength | 断点 | ASTM D-638 | 240 kg/cm |
Impact strength of cantilever beam gap | 0℃ | ASTM D-256 | 10 kg.cm/cm |
Charpy Notched Impact Strength | | ASTM D256/ISO 179 | 12 kg·cm/cm(J/M)ft·lb/in |
Rockwell hardness | | ASTM D785 | 90 |
elongation at break | | ASTM D638/ISO 527 | 200 kg/cm²(MPa)[Lb/in²] |
Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Volume resistivity | | HS Method | >10 Ω |
Physical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
melt mass-flow rate | | ASTM D1238/ISO 1133 | 0.4 g/10min |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Linear coefficient of thermal expansion | 0℃-110℃ | Dilatometor | 1.5×10 K |
vicat | | ASTM D-1525 | 150 °C |
melting temperature | | HS Method | 162 °C |
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.