ABS+PA Terblend® N NM-13 INEOS Barex
0
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.1 % |
| Tensile modulus | ISO 527-2 | 1600 MPa | |
| tensile strength | 屈服,23°C | ISO 527-2 | 35.0 MPa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 3.4 % |
| Flexural modulus | ISO 178 | 1500 MPa | |
| bending strength | ISO 178 | 50.0 MPa | |
| elongation | Break | ISO 527-3 | >50 % |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 30 kJ/m² |
| 23°C | ISO 179 | 80 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/A | 30 kJ/m² |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 58.0 °C |
| vicat | -- | ISO 306/A50 | 165 °C |
| -- | ISO 306/B50 | 91.0 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1E-04 cm/cm/°C |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 2.90 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.015 |
| density | ISO 1183 | 1.07 g/cm³ | |
| Melt volume flow rate | 240°C/10.0kg | ISO 1133 | 25.0 cm³/10min |
| Shrinkage rate | ISO 294-4 | 0.80 % | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 75 kJ/m² |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 80.0 °C |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.