Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS+PA Terblend® N NM-13 INEOS Barex
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | INEOS Barex/Terblend® N NM-13 | |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1E-04 cm/cm/°C |
| Dissipation Factor | 1MHz | IEC 60250 | 0.015 |
| Melt volume flow rate | 240°C/10.0kg | ISO 1133 | 25.0 cm³/10min |
| vicat | -- | ISO 306/B50 | 91.0 °C |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| density | ISO 1183 | 1.07 g/cm³ | |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 80.0 °C |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 80 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/A | 30 kJ/m² |
| 23°C | ISO 180/A | 75 kJ/m² | |
| Shrinkage rate | ISO 294-4 | 0.80 % | |
| bending strength | ISO 178 | 50.0 MPa | |
| relative permittivity | 1MHz | IEC 60250 | 2.90 |
| tensile strength | 屈服,23°C | ISO 527-2 | 35.0 MPa |
| Tensile modulus | ISO 527-2 | 1600 MPa | |
| vicat | -- | ISO 306/A50 | 165 °C |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Tensile strain | 屈服,23°C | ISO 527-2 | 3.4 % |
| Flexural modulus | ISO 178 | 1500 MPa | |
| elongation | 断裂 | ISO 527-3 | >50 % |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 30 kJ/m² |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 58.0 °C |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.1 % |