برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 14to45 g/10min |
| melt mass-flow rate | 260°C/5.0kg | ISO 1133 | 19to40 g/10min |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 17.0to26.0 cm³/10min |
| Shrinkage rate | MD:23°C | ASTM D955 | 0.50to0.60 % |
| Shrinkage rate | 23°C | ISO 294-4 | 0.59to0.70 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.10to0.25 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.60to1.0 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20to0.30 % |
| density | -- | ASTM D792 | 1.10to1.25 g/cm³ |
| density | 23°C | ISO 1183 | 1.11to1.20 g/cm³ |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | 23°C | ASTM D785 | 109to116 |
| ball-indentation hardness | | ISO 2039-1 | 88.7to110 MPa |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Hot filament ignition temperature | | IEC 60695-2-13 | 550to960 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 断裂,23°C | ASTM D638 | 44.0to66.0 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 39.0to64.3 MPa |
| elongation | 屈服,23°C | ASTM D638 | 3.7to6.1 % |
| elongation | 屈服,23°C | ISO 527-2 | 2.3to8.7 % |
| elongation | 断裂,23°C | ASTM D638 | 23to100 % |
| elongation | 断裂,23°C | ISO 527-2 | 36to80 % |
| Flexural modulus | 23°C | ASTM D790 | 2080to2770 MPa |
| Flexural modulus | 23°C | ISO 178 | 2000to2640 MPa |
| bending strength | 23°C | ASTM D790 | 68.0to94.0 MPa |
| bending strength | 23°C | ISO 178 | 72.8to97.5 MPa |
| bending strength | 屈服,23°C | ASTM D790 | 81.7to95.4 MPa |
| Tensile modulus | 23°C | ASTM D638 | 2540to2720 MPa |
| Tensile modulus | 23°C | ISO 527-2 | 2120to2760 MPa |
| tensile strength | 屈服,23°C | ASTM D638 | 52.9to65.6 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 54.6to62.4 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 5.0to62 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 140to600 J/m |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 16to61 kJ/m² |
| Dart impact | 23°C | ASTM D3763 | 35.3to47.9 J |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1.0E+13到1.0E+15 ohms |
| Volume resistivity | 23°C | IEC 60093 | 1.0E+13到1.0E+15 ohms·cm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD | ASTME831 | 7.2E-5到7.3E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.0E-5到8.6E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ASTME831 | 7.2E-5到7.9E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 7.1E-5到7.8E-5 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 102to130 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 98.4to132 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 87.7to113 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 87.2to122 °C |
| vicat | -- | ASTM D1525 | 104to138 °C |
| vicat | -- | ISO 306 | 102to139 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.