برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.34 g/cm³ |
| thickness | 层能力 | | 254.0to330.2 µm |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| NBSSmokeDensity | flaming | ASTMF814/E662 | Passed |
| NBSSmokeDensity | non-flaming | ASTMF814/E662 | Passed |
| OSU total heat release | 2mintest | FAR25.853 | 16.0 kW·min/m² |
| OSU total heat release | 5mintest | FAR25.853 | 36.0 kW/m² |
| UL combustion rating | 1.02到6.35mm，垂直 | FAR25.853 | 2.0 sec |
| exothermic | 1.52mm | FAR25.853 | Passed |
| UL flame retardant rating | FAA | FAR25.853 | <5.00 |
| UL flame retardant rating | | UL 94 | V-0 |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Outgassing | CollectedVolatileCondensableMaterial(CVCM) | ASTME595 | -0.10 % |
| Outgassing | TotalMassLost(TML) | ASTME595 | 0.41 % |
| Outgassing | WaterVaporRecovered(WVR) | ASTME595 | -0.37 % |
| Antifungal activity | 方法 | MILSTD-810G | Passed |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 3.18mm | ASTM D638 | 2220 MPa |
| tensile strength | 3.18mm | ASTM D638 | 71.7 MPa |
| elongation | 断裂,3.18mm | ASTM D638 | 6.0 % |
| Flexural modulus | | ASTM D790 | 2500 MPa |
| shear strength | 6.35mm | ASTM D732 | 57.2 MPa |
| bending strength | | ASTM D790 | 115 MPa |
| Compression Modulus | | ASTM D732 | 1930 MPa |
| compressive strength | | ASTM D695 | 105 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256A | 110 J/m |
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | 610 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| dielectric strength | | ASTM D149 | 4.3to11 kV/mm |
| dielectric constant | | ASTM D150 | 3.00to3.20 |
| Dissipation Factor | | ASTM D150 | 2.6E-3到2.7E-3 |
| Volume resistivity | | ASTM D257 | 6.0E+13到1.0E+14 ohms |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 153 °C |
| Glass Transition Temperature | | DSC | 367 °C |
| Linear coefficient of thermal expansion | MD | ASTME228 | 6.6E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.