برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.08 g/cm³ |
| density | | ISO 1183 | 1.08 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 1.9 g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 24.0 cm³/10min |
| Shrinkage rate | MD | ASTM D955 | 0.20to0.60 % |
| Shrinkage rate | | ISO 294-4 | 0.20to0.60 % |
| Water absorption rate | 饱和,23°C | ASTM D570 | 0.10 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 70 |
| ball-indentation hardness | | ISO 2039-1 | 168 MPa |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| refractive index | | ASTM D542 | 1.570 |
| refractive index | | ISO 489 | 1.570 |
| transmissivity | 550nm | ASTM D1003 | 91.3 % |
| Haze ratio | | ASTM D1003 | 0.30 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 21 J/m |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 2.5 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 12 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 1.5 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 12 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ASTM D638 | 3240 MPa |
| Tensile modulus | | ISO 527-2 | 3300 MPa |
| tensile strength | 屈服,23°C | ASTM D638 | 57.9 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 60.0 MPa |
| elongation | Break | ASTM D638 | 2.1 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.5 % |
| Flexural modulus | | ASTM D790 | 3100 MPa |
| Flexural modulus | | ISO 178 | 3400 MPa |
| bending strength | | ASTM D790 | 97.2 MPa |
| bending strength | | ISO 178 | 100 MPa |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 90.0 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 80.0 °C |
| vicat | | ASTM D15253 | 106 °C |
| vicat | | ISO 306/B50 | 98.0 °C |
| maximum service temperature | | | 260 °C |