برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 260°C/5.0 kg | ASTM D1238 | 22 g/10 min |
| Shrinkage rate | Flow | ASTM D955 | 0.60 - 0.65 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.8 mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | | ASTM D638 | 53.0 Mpa |
| Flexural modulus | | ASTM D790 | 2280 Mpa |
| bending strength | | ASTM D790 | 82.4 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Suspended wall beam without notch impact strength | 3.18 mm | ASTM D256 | 590 J/m |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| drying temperature | | | 100 to 110 °C |
| drying time | | | 3.0 to 5.0 hr |
| Temperature at the rear of the barrel | | | 270 to 290 °C |
| Temperature in the middle of the barrel | | | 280 to 300 °C |
| Temperature at the front of the material cylinder | | | 285 to 305 °C |
| Spray nozzle temperature | | | 295 to 315 °C |
| Temperature | | | 50 to 80 °C |
| Back pressure | | | 0.490 to 2.94 Mpa |
| screw speed | | | 30 to 50 rpm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ASTM D648 | 122 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.