برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Specific volume | | ASTM D792 | 0.830 cm³/g |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 7.0 g/10 min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Water absorption rate | 24 hr | ASTM D570 | 0.15 % |
| Water absorption rate | 平衡, 23°C | ASTM D570 | 0.35 % |
| Water absorption rate | 平衡, 100°C | ASTM D570 | 0.58 % |
| Outdoor applicability | | UL 746C | f1 |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M 级 | ASTM D785 | 70 |
| Rockwell hardness | R 级 | ASTM D785 | 118 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| refractive index | | ASTM D542 | 1.586 |
| transmissivity | 2540 µm | ASTM D1003 | 88.0 % |
| Haze ratio | 2540 µm | ASTM D1003 | 1.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.75 mm | UL 94 | V-2 |
| UL flame retardant rating | 6.0 mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 屈服 | ASTM D638 | 62.0 Mpa |
| tensile strength | 断裂 | ASTM D638 | 65.0 Mpa |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| elongation | 断裂 | ASTM D638 | 110 % |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 2340 Mpa |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 93.0 Mpa |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 mg |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 J/m |
| Dart impact | 23°C | ASTM D3029 | 169 J |
| Impact strength of cantilever beam gap | | ASTM D1822 | 546 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | > 1.0E+17 ohms·cm |
| dielectric strength | 3.20 mm, in Air | ASTM D149 | 15 KV/mm |
| dielectric constant | 60 Hz | ASTM D150 | 3.17 |
| dielectric constant | 50 kHz | ASTM D150 | 3.17 |
| dielectric constant | 1 MHz | ASTM D150 | 2.96 |
| Dissipation Factor | 50 Hz | ASTM D150 | 9.0E-4 |
| Dissipation Factor | 60 Hz | ASTM D150 | 9.0E-4 |
| Dissipation Factor | 1 MHz | ASTM D150 | 0.010 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 2 |
| High arc combustion index (HAI) | | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | | UL 746 | PLC 4 |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| drying temperature | | | 120 °C |
| drying time | | | 3.0 to 4.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Suggested injection volume | | | 40 to 60 % |
| Temperature at the rear of the barrel | | | 290 to 310 °C |
| Temperature in the middle of the barrel | | | 300 to 320 °C |
| Temperature at the front of the material cylinder | | | 310 to 330 °C |
| Spray nozzle temperature | | | 305 to 325 °C |
| Processing (melt) temperature | | | 310 to 330 °C |
| Temperature | | | 80 to 115 °C |
| Back pressure | | | 0.300 to 0.700 Mpa |
| screw speed | | | 40 to 70 rpm |
| Exhaust hole depth | | | 0.025 to 0.076 mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 137 °C |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 132 °C |
| vicat | | ASTM D15255 | 154 °C |
| Linear coefficient of thermal expansion | -40 到 95°C，流动 | ASTM E831 | 6.8E-5 cm/cm/°C |
| specific heat | | ASTM C351 | 1260 J/kg/°C |
| thermal conductivity | | ASTM C177 | 0.29 W/m/K |
| RTI Elec | | UL 746 | 130 °C |
| RTI Imp | | UL 746 | 130 °C |
| RTI | | UL 746 | 130 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.