Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 203R-111 SABIC INNOVATIVE SINGAPHORE
LEXAN™
Bottle cap、Casters
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/203R-111 |
|---|---|---|---|
| Falling hammer impact | 23°C | ASTM D3029 | 169 J |
| 23°C | ASTM D4812 | 3200 J/m | |
| Tensile impact strength 4 | ASTM D1822 | 546 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/203R-111 |
|---|---|---|---|
| Rockwell hardness | M 级 | ASTM D785 | 70 |
| R 级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/203R-111 |
|---|---|---|---|
| Tensile strength 2 | 屈服 | ASTM D638 | 62.0 Mpa |
| 断裂 | ASTM D638 | 65.0 Mpa | |
| 断裂 | ASTM D638 | 110 % | |
| 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 mg | |
| 屈服 | ASTM D638 | 7.0 % | |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 93.0 Mpa |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 2340 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/203R-111 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | > 1.0E+17 ohms·cm | |
| dielectric constant | 60 Hz | ASTM D150 | 3.17 |
| Dissipation Factor | 60 Hz | ASTM D150 | 9.0E-4 |
| 50 Hz | ASTM D150 | 9.0E-4 | |
| dielectric constant | 1 MHz | ASTM D150 | 2.96 |
| Hot wire ignition (HWI) | UL 746 | PLC 4 | |
| dielectric strength | 3.20 mm, in Air | ASTM D149 | 15 KV/mm |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| Dissipation Factor | 1 MHz | ASTM D150 | 0.010 |
| High arc combustion index (HAI) | UL 746 | PLC 1 | |
| dielectric constant | 50 kHz | ASTM D150 | 3.17 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/203R-111 |
|---|---|---|---|
| refractive index | ASTM D542 | 1.586 | |
| transmissivity | 2540 µm | ASTM D1003 | 88.0 % |
| Haze ratio | 2540 µm | ASTM D1003 | 1.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/203R-111 |
|---|---|---|---|
| UL flame retardant rating | 6.0 mm | UL 94 | V-0 |
| 0.75 mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/203R-111 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C | ASTM D570 | 0.35 % |
| 平衡, 100°C | ASTM D570 | 0.58 % | |
| Outdoor applicability | UL 746C | f1 | |
| Water absorption rate | 24 hr | ASTM D570 | 0.15 % |
| Specific volume | ASTM D792 | 0.830 cm³/g | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 7.0 g/10 min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/203R-111 |
|---|---|---|---|
| -40 到 95°C | ASTM E831 | 6.8E-5 cm/cm/°C | |
| thermal conductivity | ASTM C177 | 0.29 W/m/K | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 137 °C |
| vicat | ASTM D15255 | 154 °C | |
| specific heat | ASTM C351 | 1260 J/kg/°C | |
| RTI Imp | UL 746 | 130 °C | |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 132 °C |
| RTI | UL 746 | 130 °C | |
| RTI Elec | UL 746 | 130 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/203R-111 |
|---|---|---|---|
| Processing (melt) temperature | 310 到 330 °C | ||
| drying temperature | 120 °C | ||
| Exhaust hole depth | 0.025 到 0.076 mm | ||
| Temperature at the front of the material cylinder | 310 到 330 °C | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 300 到 320 °C | ||
| Temperature | 80 到 115 °C | ||
| screw speed | 40 到 70 rpm | ||
| Temperature at the rear of the barrel | 290 到 310 °C | ||
| Back pressure | 0.300 到 0.700 Mpa | ||
| drying time | 3.0 到 4.0 hr | ||
| Suggested injection volume | 40 到 60 % | ||
| Spray nozzle temperature | 305 到 325 °C |