| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.06 g/cm³ |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 18 g/10min |
| Shrinkage rate | | 内部方法 | 1.4 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 775 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation | Break | ASTM D638 | 5.0 % |
| Flexural modulus | | ASTM D790 | 1900 MPa |
| tensile strength | Yield | ASTM D638 | 20.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 2.2 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 35 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| needle flame test | | IEC 60695-11-5 | Pass |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 65.0 °C |
| vicat | | ASTM D15252 | 78.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.