PBT TAROLOX 10 G3 X0 Taro Plast S.p.A.

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	TD	ASTM D955	0.80to1.0 %
Water absorption rate	23°C,24hr	ASTMD570	0.050 %
	Water absorption rate	Saturation	ASTM D570	0.30 %
	Water absorption rate	Water absorption rate	饱和,23°C	ISO 62	0.30 %
density		ASTMD792	1.52to1.54 g/cm³
Shrinkage rate	MD	ASTM D955	0.50to0.80 %
GranuleHumidity		内部方法	<0.050 %
Water absorption rate	饱和,23°C	ISO 62	0.30 %
Shrinkage rate	TD	ASTM D955	0.80to1.0 %
Water absorption rate	Saturation	ASTM D570	0.30 %
GranuleHumidity		内部方法	<0.050 %
Water absorption rate	23°C,24hr	ASTMD570	0.050 %
density		ASTMD792	1.52to1.54 g/cm³
Shrinkage rate	MD	ASTM D955	0.50to0.80 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	R-Scale	ASTM D785	118
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	118

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot filament ignition temperature		IEC 60695-2-13	775 °C
Limiting Oxygen Index		ASTM D2863	28 %
UL flame retardant rating	1.0mm	UL 94	V-0
Limiting Oxygen Index		ASTM D2863	28 %
Hot filament ignition temperature		IEC 60695-2-13	775 °C
Burning wire flammability index	2.0mm	IEC 60695-2-12	960 °C
UL flame retardant rating	1.6mm	UL 94	V-0
	UL flame retardant rating	3.2mm	UL 94	V-0
		UL flame retardant rating	1.0mm	UL 94	V-0
			UL flame retardant rating	1.6mm	UL 94	V-0
			UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	V-0
Burning wire flammability index	2.0mm	IEC 60695-2-12	960 °C

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C,3.20mm	ASTMD256	60 J/m
Charpy Notched Impact Strength	23°C	ISO 179	4.5 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	4.5 kJ/m²
Impact strength of cantilever beam gap	23°C,3.20mm	ASTMD256	60 J/m

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTMD638	5500 MPa
tensile strength	Break	ASTMD638	95.0 MPa
elongation	Break	ASTMD638	4.0 %
Flexural modulus		ASTMD790	5500 MPa
bending strength	--	ISO 178	140 MPa
bending strength	bending strength	Break	ASTM D790	140 MPa
Tensile modulus		ASTMD638	5500 MPa
bending strength	Break	ASTM D790	140 MPa
elongation	Break	ASTMD638	4.0 %
bending strength	--	ISO 178	140 MPa
Flexural modulus		ASTMD790	5500 MPa
tensile strength	Break	ASTMD638	95.0 MPa

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
dielectric strength	2.00mm	ASTM D149	22 kV/mm
Compared to the Leakage Tracking Index (CTI)	解决方案A	IEC 60112	PLC 2
Compared to the Leakage Tracking Index (CTI)	Compared to the Leakage Tracking Index (CTI)	解决方案B	IEC 60112	PLC 3
Volume resistivity		ASTM D257	>1.0E+15 ohms·cm
Volume resistivity	Volume resistivity		ASTM D257	>1.0E+15 ohms·cm
dielectric strength	2.00mm	ASTM D149	22 kV/mm
Compared to the Leakage Tracking Index (CTI)	解决方案A	IEC 60112	PLC 2
Compared to the Leakage Tracking Index (CTI)	Compared to the Leakage Tracking Index (CTI)	解决方案B	IEC 60112	PLC 3

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,未退火，HDT	ASTMD648	210 °C
Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火，HDT	ASTMD648	190 °C
Continuous use temperature	--	UL 746B	75.0 °C
	Continuous use temperature	--4	IEC 60216	90.0 °C
		Continuous use temperature	--5	IEC 60216	120 °C
			Continuous use temperature	--6	IEC 60216	130 °C
			Continuous use temperature	Continuous use temperature	--7	IEC 60216	160 °C
vicat	--	ASTMD15258	210 °C
vicat	vicat	--	ASTMD15259	205 °C
ball-indentation hardness	215°C	VDE0470	通过
Linear coefficient of thermal expansion	MD：-30到30°C	ASTM D696	3E-05 cm/cm/°C
vicat	--	ASTMD15259	205 °C
Continuous use temperature	--5	IEC 60216	120 °C
Continuous use temperature	Continuous use temperature	--4	IEC 60216	90.0 °C
Heat distortion temperature	1.8MPa,未退火，HDT	ASTMD648	190 °C
vicat	--	ASTMD15258	210 °C
ball-indentation hardness	215°C	VDE0470	通过
Continuous use temperature	--	UL 746B	75.0 °C
Heat distortion temperature	0.45MPa,未退火，HDT	ASTMD648	210 °C
Continuous use temperature	--7	IEC 60216	160 °C
Continuous use temperature	Continuous use temperature	--6	IEC 60216	130 °C
melting temperature		ASTMD211	220to225 °C
melting temperature	melting temperature		ASTMD211	220to225 °C
Linear coefficient of thermal expansion	MD：-30到30°C	ASTM D696	3E-05 cm/cm/°C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.