PBT TAROLOX 10 G3 X0 Taro Plast S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 G3 X0 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 4.5 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 60 J/m |
| hardness | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 G3 X0 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 G3 X0 |
|---|---|---|---|
| Flexural modulus | ASTMD790 | 5500 MPa | |
| elongation | 断裂 | ASTMD638 | 4.0 % |
| bending strength | 断裂 | ASTM D790 | 140 MPa |
| Tensile modulus | ASTMD638 | 5500 MPa | |
| tensile strength | 断裂 | ASTMD638 | 95.0 MPa |
| bending strength | -- | ISO 178 | 140 MPa |
| Electrical performance | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 G3 X0 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| dielectric strength | 2.00mm | ASTM D149 | 22 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| 解决方案B | IEC 60112 | PLC 3 |
| flammability | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 G3 X0 |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 775 °C | |
| UL flame retardant rating | 1.0mm | UL 94 | V-0 |
| 3.2mm | UL 94 | V-0 | |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| Limiting Oxygen Index | ASTM D2863 | 28 % |
| physical property | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 G3 X0 |
|---|---|---|---|
| Water absorption rate | 饱和 | ASTM D570 | 0.30 % |
| Shrinkage rate | MD | ASTM D955 | 0.50to0.80 % |
| GranuleHumidity | 内部方法 | <0.050 % | |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.050 % |
| density | ASTMD792 | 1.52to1.54 g/cm³ | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.30 % |
| Shrinkage rate | TD | ASTM D955 | 0.80to1.0 % |
| Thermal performance | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 G3 X0 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTMD648 | 190 °C |
| 0.45MPa,未退火，HDT | ASTMD648 | 210 °C | |
| vicat | -- | ASTMD15259 | 205 °C |
| ball-indentation hardness | 215°C | VDE0470 | 通过 |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 3E-05 cm/cm/°C |
| Continuous use temperature | -- | UL 746B | 75.0 °C |
| --5 | IEC 60216 | 120 °C | |
| --4 | IEC 60216 | 90.0 °C | |
| --7 | IEC 60216 | 160 °C | |
| melting temperature | ASTMD211 | 220to225 °C | |
| Continuous use temperature | --6 | IEC 60216 | 130 °C |
| vicat | -- | ASTMD15258 | 210 °C |