PC 3503 Trinseo

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.20 g/cm³
Shrinkage rate	MD	ISO 294-4	0.50 %
Water absorption rate	23°C,24hr	ASTM D570	0.15 %
	Water absorption rate	23°C,24hr	ISO 62	0.15 %
		Water absorption rate	平衡,23°C,50%RH	ASTM D570	0.32 %
		Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.32 %
Shrinkage rate	MD	ASTM D955	0.50 %
melt mass-flow rate	300°C/1.2kg	ISO 1133	35 g/10min
melt mass-flow rate	melt mass-flow rate	300°C/1.2kg	ASTM D1238	35 g/10min
density		ISO 1183/B	1.20 g/cm³

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
refractive index		ASTM D542	1.586
refractive index	refractive index		ISO 489	1.586
transmissivity		ASTM D1003	89.0 %
Haze ratio		ASTM D1003	1.0 %

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	775 °C
Limiting Oxygen Index		ISO 4589-2	26 %
Burning wire flammability index	1.0mm	IEC 60695-2-12	900 °C
	Burning wire flammability index	2.0mm	IEC 60695-2-12	875 °C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	875 °C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	800 °C
Hot filament ignition temperature	Hot filament ignition temperature	2.0mm	IEC 60695-2-13	775 °C
UL flame retardant rating	1.0mm	UL 94	V-2
	UL flame retardant rating	1.5mm	UL 94	V-2
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-2

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTM D638	2300 MPa
Flexural modulus		ISO 178	2400 MPa
bending strength		ASTM D790	97.0 MPa
Tensile modulus		ISO 527-2/50	2300 MPa
tensile strength	Yield	ASTM D638	60.0 MPa
	tensile strength	Yield	ISO 527-2/50	60.0 MPa
		tensile strength	Break	ASTM D638	71.0 MPa
		tensile strength	tensile strength	Break	ISO 527-2/50	71.0 MPa
elongation	Yield	ASTM D638	6.0 %
bending strength		ISO 178	97.0 MPa
Flexural modulus		ASTM D790	2400 MPa
Tensile strain	Break	ISO 527-2/50	110 %
elongation	Break	ASTM D638	110 %
Tensile strain	Yield	ISO 527-2/50	6.0 %

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C	ISO 180/A	69 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	1800 J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	15 kJ/m²

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
dielectric strength		ASTM D149	17 kV/mm
dielectric strength	dielectric strength		IEC 60243-1	17 kV/mm
dielectric constant	60Hz	ASTM D150	3.00
dielectric constant	dielectric constant	1MHz	ASTM D150	3.00
Dissipation Factor	50Hz	ASTM D150	1E-03
Dissipation Factor	Dissipation Factor	1MHz	ASTM D150	2E-03
Compared to the Leakage Tracking Index (CTI)	2.00mm,SolutionA	IEC 60112	PLC 2

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
vicat		ISO 306/B50	145 °C
Ball pressure temperature		IEC 60335-1	>125 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05 cm/cm/°C
Heat distortion temperature	1.8MPa,退火，HDT	ISO 75-2/A	138 °C
	Heat distortion temperature	1.8MPa,退火，HDT	ASTM D648	140 °C
		Heat distortion temperature	0.45MPa,退火，HDT	ISO 75-2/B	141 °C
		Heat distortion temperature	Heat distortion temperature	0.45MPa,退火，HDT	ASTM D648	141 °C
vicat		ASTM D15255	145 °C