Impact resistance | Test Condition | Test Method | Trinseo/3503 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 15 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ASTM D256 | 1800 J/m |
23°C | ISO 180/A | 69 kJ/m² |
Mechanical properties | Test Condition | Test Method | Trinseo/3503 |
---|---|---|---|
elongation | 屈服 | ASTM D638 | 6.0 % |
tensile strength | 屈服 | ASTM D638 | 60.0 MPa |
Flexural modulus | ISO 178 | 2400 MPa | |
bending strength | ASTM D790 | 97.0 MPa | |
Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
bending strength | ISO 178 | 97.0 MPa | |
tensile strength | 屈服 | ISO 527-2/50 | 60.0 MPa |
elongation | 断裂 | ASTM D638 | 110 % |
Flexural modulus | ASTM D790 | 2400 MPa | |
Tensile modulus | ASTM D638 | 2300 MPa | |
tensile strength | 断裂 | ASTM D638 | 71.0 MPa |
Tensile modulus | ISO 527-2/50 | 2300 MPa | |
Tensile strain | 断裂 | ISO 527-2/50 | 110 % |
tensile strength | 断裂 | ISO 527-2/50 | 71.0 MPa |
Electrical performance | Test Condition | Test Method | Trinseo/3503 |
---|---|---|---|
Dissipation Factor | 50Hz | ASTM D150 | 1E-03 |
dielectric strength | IEC 60243-1 | 17 kV/mm | |
dielectric constant | 60Hz | ASTM D150 | 3.00 |
Compared to the Leakage Tracking Index (CTI) | 2.00mm,SolutionA | IEC 60112 | PLC 2 |
dielectric strength | ASTM D149 | 17 kV/mm | |
Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
Dissipation Factor | 1MHz | ASTM D150 | 2E-03 |
dielectric constant | 1MHz | ASTM D150 | 3.00 |
optical performance | Test Condition | Test Method | Trinseo/3503 |
---|---|---|---|
transmissivity | ASTM D1003 | 89.0 % | |
refractive index | ASTM D542 | 1.586 | |
Haze ratio | ASTM D1003 | 1.0 % | |
refractive index | ISO 489 | 1.586 |
flammability | Test Condition | Test Method | Trinseo/3503 |
---|---|---|---|
Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 875 °C |
Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 775 °C |
UL flame retardant rating | 3.0mm | UL 94 | V-2 |
Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 775 °C |
1.0mm | IEC 60695-2-13 | 800 °C | |
UL flame retardant rating | 1.0mm | UL 94 | V-2 |
Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 900 °C |
Limiting Oxygen Index | ISO 4589-2 | 26 % | |
Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 875 °C |
UL flame retardant rating | 1.5mm | UL 94 | V-2 |
physical property | Test Condition | Test Method | Trinseo/3503 |
---|---|---|---|
Shrinkage rate | MD | ASTM D955 | 0.50 % |
MD | ISO 294-4 | 0.50 % | |
Water absorption rate | 平衡,23°C,50%RH | ASTM D570 | 0.32 % |
density | ISO 1183/B | 1.20 g/cm³ | |
Water absorption rate | 23°C,24hr | ISO 62 | 0.15 % |
平衡,23°C,50%RH | ISO 62 | 0.32 % | |
23°C,24hr | ASTM D570 | 0.15 % | |
density | ASTM D792 | 1.20 g/cm³ | |
melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 35 g/10min |
300°C/1.2kg | ISO 1133 | 35 g/10min |
Thermal performance | Test Condition | Test Method | Trinseo/3503 |
---|---|---|---|
Ball pressure temperature | IEC 60335-1 | >125 °C | |
Heat distortion temperature | 1.8MPa,退火,HDT | ASTM D648 | 140 °C |
vicat | ISO 306/B50 | 145 °C | |
Heat distortion temperature | 1.8MPa,退火,HDT | ISO 75-2/A | 138 °C |
vicat | ASTM D15255 | 145 °C | |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
Heat distortion temperature | 0.45MPa,退火,HDT | ASTM D648 | 141 °C |
0.45MPa,退火,HDT | ISO 75-2/B | 141 °C |