ABS+PET Starex EG-7000 LOTTE KOREA

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.08 g/cm³
density	density		ISO 1183	1.08 g/cm³
melt mass-flow rate	250°C/10.0kg	ASTM D1238	35 g/10min
melt mass-flow rate	melt mass-flow rate	250°C/10.0kg	ISO 1133	35 g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.44to0.54 %
	Shrinkage rate	TD：3.20mm	ASTM D955	0.46to0.57 %
		Shrinkage rate	TD:3.20mm	ISO 2577	0.46to0.57 %
		Shrinkage rate	Shrinkage rate	MD:3.20mm	ISO 2577	0.44to0.54 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	R-Scale	ASTM D785	95
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	95

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Yellowness Index	3.20mm	ASTM D1925	20 YI

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	1.5mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTM D638	1830 MPa
Tensile modulus	Tensile modulus		ISO 527-2/50	2000 MPa
tensile strength	Yield	ASTM D638	38.2 MPa
	tensile strength	Yield	ISO 527-2/50	38.0 MPa
		tensile strength	Break	ASTM D638	28.4 MPa
		tensile strength	tensile strength	Break	ISO 527-2/50	26.0 MPa
elongation	Break	ASTM D638	40 %
Tensile strain	Break	ISO 527-2/50	18 %
Flexural modulus		ASTM D790	1960 MPa
Flexural modulus	Flexural modulus		ISO 178	1960 MPa
bending strength		ASTM D790	55.9 MPa
bending strength	bending strength		ISO 178	55.0 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	23°C	ISO 179/1eA	20 kJ/m²
Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	210 J/m
	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	200 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	21 kJ/m²

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,Annealed,4.00mm，HDT	ISO 75-2/B	97.0 °C
vicat	--	ISO 306/B50	90.0 °C
vicat	vicat	--	ISO 306/B120	91.0 °C
Heat distortion temperature	0.45MPa,Unannealed,4.00mm，HDT	ISO 75-2/B	78.0 °C
	Heat distortion temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	78.0 °C
		Heat distortion temperature	1.8MPa,未退火,6.40mm，HDT	ASTM D648	78.0 °C
			Heat distortion temperature	1.8MPa,Unannealed,4.00mm，HDT	ISO 75-2/A	78.0 °C
			Heat distortion temperature	Heat distortion temperature	1.8MPa,Annealed,4.00mm，HDT	ISO 75-2/A	88.0 °C