Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS+PET Starex EG-7000 LOTTE KOREA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LOTTE KOREA/Starex EG-7000 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 200 J/m |
| 23°C | ISO 180/1A | 21 kJ/m² | |
| 23°C,3.18mm | ASTM D256 | 210 J/m |
| hardness | Test Condition | Test Method | LOTTE KOREA/Starex EG-7000 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 95 |
| R级 | ASTM D785 | 95 |
| Mechanical properties | Test Condition | Test Method | LOTTE KOREA/Starex EG-7000 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 40 % |
| Tensile modulus | ASTM D638 | 1830 MPa | |
| tensile strength | 断裂 | ASTM D638 | 28.4 MPa |
| Flexural modulus | ASTM D790 | 1960 MPa | |
| Tensile modulus | ISO 527-2/50 | 2000 MPa | |
| tensile strength | 屈服 | ASTM D638 | 38.2 MPa |
| Flexural modulus | ISO 178 | 1960 MPa | |
| bending strength | ASTM D790 | 55.9 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 18 % |
| tensile strength | 屈服 | ISO 527-2/50 | 38.0 MPa |
| bending strength | ISO 178 | 55.0 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 26.0 MPa |
| optical performance | Test Condition | Test Method | LOTTE KOREA/Starex EG-7000 |
|---|---|---|---|
| Yellowness Index | 3.20mm | ASTM D1925 | 20 YI |
| flammability | Test Condition | Test Method | LOTTE KOREA/Starex EG-7000 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | LOTTE KOREA/Starex EG-7000 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.44to0.54 % |
| TD:3.20mm | ISO 2577 | 0.46to0.57 % | |
| TD：3.20mm | ASTM D955 | 0.46to0.57 % | |
| density | ASTM D792 | 1.08 g/cm³ | |
| melt mass-flow rate | 250°C/10.0kg | ASTM D1238 | 35 g/10min |
| density | ISO 1183 | 1.08 g/cm³ | |
| melt mass-flow rate | 250°C/10.0kg | ISO 1133 | 35 g/10min |
| Shrinkage rate | MD:3.20mm | ISO 2577 | 0.44to0.54 % |
| Thermal performance | Test Condition | Test Method | LOTTE KOREA/Starex EG-7000 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 78.0 °C |
| vicat | -- | ISO 306/B120 | 91.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 78.0 °C |
| 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 78.0 °C | |
| 1.8MPa,Annealed,4.00mm，HDT | ISO 75-2/A | 88.0 °C | |
| vicat | -- | ISO 306/B50 | 90.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 78.0 °C |
| 0.45MPa,Annealed,4.00mm，HDT | ISO 75-2/B | 97.0 °C |