SBC Generic SBC Generic

مقایسه

برگه داده فنی

	شرایط آزمون	روش آزمون	نتیجه آزمون
density	--	ASTM D792	0.898to1.07 g/cm³
density	density	23°C	ISO 1183	0.886to1.09 g/cm³
melt mass-flow rate	200°C/5.0kg	ASTM D1238	1.0to15 g/10min
melt mass-flow rate	melt mass-flow rate	200°C/5.0kg	ISO 1133	3.4to8.0 g/10min
Melt volume flow rate	200°C/5.0kg	ISO 1133	10.9to12.1 cm³/10min
Shrinkage rate	MD:23°C	ASTM D955	0.60to0.68 %
Shrinkage rate	Shrinkage rate	23°C	ISO 294-4	0.50to2.4 %
Shore hardness	23°C	ASTM D2240	47to92
Shore hardness	Shore hardness	23°C	ISO 868	39to91
Flexural modulus	23°C	ASTM D790	1330to1800 MPa
Flexural modulus	Flexural modulus	23°C	ISO 178	1380to2460 MPa
bending strength	23°C	ISO 178	16.5to76.5 MPa
bending strength	bending strength	屈服,23°C	ASTM D790	24.4to54.0 MPa
tensile strength	100%应变,23°C	ISO 37	1.80to5.38 MPa
	tensile strength	屈服,23°C	ASTM D638	1.03to33.4 MPa
		tensile strength	200%应变,23°C	ISO 37	1.70to6.90 MPa
			tensile strength	300%应变,23°C	ASTM D412	2.00to4.57 MPa
				tensile strength	300%应变,23°C	ISO 37	1.00to8.00 MPa
				tensile strength	tensile strength	屈服,23°C	ISO 37	1.70to33.0 MPa
Haze ratio		ASTM D1003	0.20to3.1 %
tensile strength	屈服,23°C	ISO 527-2	4.00to51.0 MPa
tensile strength	tensile strength	断裂,23°C	ISO 527-2	14.0to64.0 MPa
Tensile strain	屈服,23°C	ISO 527-2	2.0to2.1 %
Tensile strain	Tensile strain	断裂,23°C	ASTM D638	30to260 %
Nominal tensile fracture strain	23°C	ISO 527-2	2.5to500 %
tensile strength	断裂,23°C	ASTM D412	3.96to20.3 MPa
elongation	断裂,23°C	ASTM D412	550to850 %
elongation	elongation	断裂,23°C	ISO 37	400to890 %
tear strength	23°C	ASTM D624	19.8to104 kN/m
tear strength	tear strength	23°C	ISO 34-1	18to110 kN/m
compression set	23°C	ISO 815	18to36 %
Charpy Notched Impact Strength	23°C	ISO 179	1.6to9.9 kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	20to110 J/m
Dart impact	23°C	ASTM D3763	0.602to41.6 J
Maximum continuous use temperature		SAEJ2236	150to170 °C
Heat distortion temperature	1.8MPa,未退火，HDT	ASTM D648	59.6to62.7 °C
brittle temperature		ASTM D746	-60.0--59.0 °C
vicat	--	ASTM D1525	62.7to90.0 °C
vicat	vicat	--	ISO 306	62.0to93.5 °C
burning rate		ISO 3795	37to54 mm/min
transmissivity		ASTM D1003	88.9to93.1 %

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.