PC 2081-12

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTMD792	1.20 g/cm³
melt mass-flow rate	300°C/1.2kg	ASTMD1238	12 g/10min
Shrinkage rate	MD	ASTM D955	0.50to0.70 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.50to0.70 %
Water absorption rate	23°C,24hr	ASTMD570	0.15 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ASTMD570	0.32 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	M-Scale	ASTM D785	73
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	118

optical performance	روش آزمون	نتیجه آزمون
refractive index	ASTMD542	1.586
transmissivity	ASTM D1003	85.0 %
Haze ratio	ASTM D1003	1.0 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
bending strength	--3	ASTM D790	100 MPa
bending strength	bending strength	--4,5	ISO 178	95.8 MPa
Abrasion		ASTM D1044	45 %
Tensile modulus	--2	ASTM D638	2270 MPa
Tensile modulus	Tensile modulus	--	ISO 527-2/50	2300 MPa
tensile strength	屈服2	ASTM D638	64.3 MPa
	tensile strength	Yield	ISO 527-2/50	65.2 MPa
		tensile strength	断裂2	ASTM D638	69.1 MPa
		tensile strength	tensile strength	Break	ISO 527-2/50	69.6 MPa
elongation	屈服2	ASTM D638	6.3 %
	elongation	Yield	ISO 527-2/50	6.1 %
		elongation	断裂2	ASTM D638	150 %
		elongation	elongation	Break	ISO 527-2/50	150 %
Flexural modulus	--3	ASTM D790	2200 MPa
Flexural modulus	Flexural modulus	--4,5	ISO 178	2300 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	23°C	ISO 179/1eA	25 kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	750 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/A	65 kJ/m²
Suspended wall beam without notch impact strength	23°C	ASTMD256	无断裂
Dart impact	23°C,总能量	ASTM D3763	86.9 J
Impact strength of cantilever beam gap		ASTM D1822	378 kJ/m²

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Dissipation Factor	50Hz	ASTM D150	1E-03
Dissipation Factor	Dissipation Factor	1MHz	ASTM D150	2E-03
Volume resistivity		ASTM D257	2E+17 ohms·cm
dielectric strength		ASTMD149	17 kV/mm
dielectric constant	60Hz	ASTM D150	3.00
dielectric constant	dielectric constant	1MHz	ASTM D150	3.00

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	1.8MPa,未退火，HDT	ASTM D648	121 °C
	Heat distortion temperature	1.8MPa,未退火，HDT	ISO 75-2/A	123 °C
	Heat distortion temperature	Heat distortion temperature	1.8MPa,退火，HDT	ASTM D648	125 °C
vicat		ISO 306/B50	141 °C
Linear coefficient of thermal expansion	MD：-40到82°C	ASTM D696	6.8E-05 cm/cm/°C
Heat distortion temperature	0.45MPa,退火，HDT	ASTM D648	134 °C