برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | 24hr | ISO 62 | 0.5 % |
| Shrinkage rate | | ISO 294-4 | 1.7 % |
| melt mass-flow rate | 230℃/2.16 kg | ISO 1133 | 20 g/10 min |
| Shrinkage rate | | ISO 294-4 | 1.3 % |
| Water absorption rate | 23℃, 24 hr | ISO 62 | 0.30 % |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shore hardness | 邵氏 D | ISO 868 | 63 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | | ISO 527 | 36 Mpa |
| elongation at break | | ISO 527 | 460 % |
| Flexural elasticity | | ISO 178 | 300 Mpa |
| Impact strength of cantilever beam gap | | ISO 179/IeA | PARTIAL BREAK kJ/㎡ |
| Volume resistivity | | IEC 60093 | 7.0E 13 Ohm cm |
| Volume resistivity | | IEC 60093 | 3.0E 13 Ohm |
| dielectric strength | | IEC 60243 | 17 KV/mm |
| Shore hardness | 邵氏 D | ISO 868 | 63 |
| tensile strength | 屈服 | ISO 527-2 | 40.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 460 % |
| Flexural modulus | | ISO 178 | 350 Mpa |
| Charpy Notched Impact Strength | | ISO 179/1eA | 无断裂 |
| Other performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | | ISO 527 | 36 Mpa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 2.8E+15 Ohm |
| Volume resistivity | | IEC 60093 | 6.3E+13 ohm·cm |
| dielectric strength | 2.00 mm | IEC 60243-1 | 17 KV/mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melting temperature | | ISO 3146C | 211 °C |
| melt mass-flow rate | 2.16kg at 230℃ | ISO 1133 | 8 g/10 min |
| melting temperature | | ISO 3146 | 212 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.