physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Melt volume flow rate | 300°C/10.0kg | ISO 1133 | 30.0 cm³/10min |
Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 9.00 cm³/10min |
Shrinkage rate | TD:24小时 | ISO 294-4 | 0.60to0.80 % |
Shrinkage rate | MD:24小时 | ISO 294-4 | 0.60to0.80 % |
Water absorption rate | 23°C,24hr | ISO 62 | 0.030 % |
density | | ISO 1183 | 1.35 g/cm³ |
melt mass-flow rate | 300°C/10.0kg | ASTM D1238 | 36 g/10min |
melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 11 g/10min |
flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
UL flame retardant rating | 1.030mm | UL 94 | HB |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
tensile strength | Yield | ISO 527-2/50 | 56.0 MPa |
tensile strength | 断裂3 | ASTM D638 | 46.0 MPa |
tensile strength | Break | ISO 527-2/50 | 49.0 MPa |
elongation | 屈服3 | ASTM D638 | 8.7 % |
elongation | Yield | ISO 527-2/50 | 7.9 % |
elongation | 断裂3 | ASTM D638 | 14 % |
elongation | Break | ISO 527-2/50 | 16 % |
Flexural modulus | 50.0mm跨距4 | ASTM D790 | 2350 MPa |
Flexural modulus | --5 | ISO 178 | 2620 MPa |
Tensile modulus | --2 | ASTM D638 | 2530 MPa |
Tensile modulus | -- | ISO 527-2/1 | 2490 MPa |
tensile strength | 屈服3 | ASTM D638 | 55.0 MPa |
bending strength | --5,6 | ISO 178 | 95.0 MPa |
bending strength | --5,7 | ISO 178 | 93.0 MPa |
bending strength | 屈服,50.0mm跨距4 | ASTM D790 | 85.0 MPa |
bending strength | 断裂,50.0mm跨距4 | ASTM D790 | 83.0 MPa |
Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Impact strength of cantilever beam gap | -20°C | ASTM D256 | 150 J/m |
Impact strength of cantilever beam gap | 23°C | ASTM D256 | 280 J/m |
Impact strength of cantilever beam gap | -20°C8 | ISO 180/1A | 13 kJ/m² |
Impact strength of cantilever beam gap | 23°C8 | ISO 180/1A | 30 kJ/m² |
Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Dissipation Factor | 1.10GHz | 内部方法 | 9E-04 |
Dissipation Factor | 1.90GHz | 内部方法 | 1.1E-03 |
Dissipation Factor | 5.00GHz | 内部方法 | 1.9E-03 |
Dissipation Factor | 10.0GHz | 内部方法 | 2.2E-03 |
dielectric constant | 1.10GHz | 内部方法 | 3.56 |
dielectric constant | 1.90GHz | 内部方法 | 3.57 |
dielectric constant | 5.00GHz | 内部方法 | 3.57 |
dielectric constant | 10.0GHz | 内部方法 | 3.58 |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Heat distortion temperature | 0.45MPa,未退火,3.20mm,HDT | ASTM D648 | 173 °C |
Heat distortion temperature | 0.45MPa,未退火,64.0mm跨距9,HDT | ISO 75-2/Bf | 173 °C |
Heat distortion temperature | 1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 154 °C |
Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距9,HDT | ISO 75-2/Af | 155 °C |
Linear coefficient of thermal expansion | MD:-40到150°C | ASTME831 | 6.1E-05 cm/cm/°C |
Linear coefficient of thermal expansion | TD:-40到150°C | ASTME831 | 8.7E-05 cm/cm/°C |