PPO(PPE)+SEBS LNP™ THERMOCOMP™ ZKC06 compound SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/LNP™ THERMOCOMP™ ZKC06 compound |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 280 J/m |
| 23°C8 | ISO 180/1A | 30 kJ/m² | |
| -20°C | ASTM D256 | 150 J/m | |
| -20°C8 | ISO 180/1A | 13 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC/LNP™ THERMOCOMP™ ZKC06 compound |
|---|---|---|---|
| tensile strength | 屈服3 | ASTM D638 | 55.0 MPa |
| elongation | 断裂3 | ASTM D638 | 14 % |
| 断裂 | ISO 527-2/50 | 16 % | |
| Flexural modulus | --5 | ISO 178 | 2620 MPa |
| bending strength | 断裂,50.0mm跨距4 | ASTM D790 | 83.0 MPa |
| Tensile modulus | -- | ISO 527-2/1 | 2490 MPa |
| bending strength | 屈服,50.0mm跨距4 | ASTM D790 | 85.0 MPa |
| tensile strength | 屈服 | ISO 527-2/50 | 56.0 MPa |
| Flexural modulus | 50.0mm跨距4 | ASTM D790 | 2350 MPa |
| bending strength | --5,7 | ISO 178 | 93.0 MPa |
| --5,6 | ISO 178 | 95.0 MPa | |
| elongation | 屈服 | ISO 527-2/50 | 7.9 % |
| 屈服3 | ASTM D638 | 8.7 % | |
| tensile strength | 断裂3 | ASTM D638 | 46.0 MPa |
| 断裂 | ISO 527-2/50 | 49.0 MPa | |
| Tensile modulus | --2 | ASTM D638 | 2530 MPa |
| Electrical performance | Test Condition | Test Method | SABIC/LNP™ THERMOCOMP™ ZKC06 compound |
|---|---|---|---|
| dielectric constant | 1.90GHz | 内部方法 | 3.57 |
| Dissipation Factor | 5.00GHz | 内部方法 | 1.9E-03 |
| 1.90GHz | 内部方法 | 1.1E-03 | |
| 10.0GHz | 内部方法 | 2.2E-03 | |
| dielectric constant | 1.10GHz | 内部方法 | 3.56 |
| Dissipation Factor | 1.10GHz | 内部方法 | 9E-04 |
| dielectric constant | 10.0GHz | 内部方法 | 3.58 |
| 5.00GHz | 内部方法 | 3.57 |
| flammability | Test Condition | Test Method | SABIC/LNP™ THERMOCOMP™ ZKC06 compound |
|---|---|---|---|
| UL flame retardant rating | 1.030mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC/LNP™ THERMOCOMP™ ZKC06 compound |
|---|---|---|---|
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 9.00 cm³/10min |
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.60to0.80 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.030 % |
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 11 g/10min |
| Melt volume flow rate | 300°C/10.0kg | ISO 1133 | 30.0 cm³/10min |
| Shrinkage rate | TD:24小时 | ISO 294-4 | 0.60to0.80 % |
| density | ISO 1183 | 1.35 g/cm³ | |
| melt mass-flow rate | 300°C/10.0kg | ASTM D1238 | 36 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC/LNP™ THERMOCOMP™ ZKC06 compound |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,64.0mm跨距9，HDT | ISO 75-2/Bf | 173 °C |
| Linear coefficient of thermal expansion | MD:-40到150°C | ASTME831 | 6.1E-05 cm/cm/°C |
| TD:-40到150°C | ASTME831 | 8.7E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 173 °C |
| 1.8MPa,未退火,64.0mm跨距9，HDT | ISO 75-2/Af | 155 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 154 °C |