| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | | ASTM D1238 | 35 g/10min |
| Melt volume flow rate | | ISO 1133 | 11 cm³/10 min |
| Shrinkage rate | flow, 3.2 | Internal | 0.7-1 |
| Water absorption rate | 23°C/sat | ISO 62 | 0.1 |
| Water absorption rate | 23°C / 50 | ISO 62 | 0.03 |
| Thermal Properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| vicat | Rate B/50 | ASTM D1525 | 105 °C |
| vicat | Rate B/5 | ISO 306 | 123 °C |
| vicat | Rate B/5 | ISO 306 | 121 °C |
| RTI Imp | | UL 746B | 120 °C |
| RTI Elec | | UL 746B | 120 °C |
| RTI Imp | | UL 746B | 120 °C |
| Linear coefficient of thermal expansion | -40°C to 4，流动 | ASTM E831 | 88.4 E-6 °C |
| Linear coefficient of thermal expansion | -40°C to 4，流动 | ISO 11359-2 | 88.4 E-6 °C |
| Linear coefficient of thermal expansion | -40°C to 4，横向 | ASTM E831 | 89.7 E-6 °C |
| Linear coefficient of thermal expansion | -40°C to 4，横向 | ISO 11359-2 | 89.7 E-6 °C |
| Ball indentation temperature | Pass | IEC 60695-10-2 | 75 °C |
| Ball indentation temperature | Pass | IEC 60695-10-2 | 125 °C |
| combustibility | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL fire rating V | | UL 94 | 1.5 mm |
| UL flame retardant rating | 5VA | UL 94 | 3 mm |
| Glow wire combustion index (GWFI) | 1mm | IEC 60695-2-12 | 960 passes at |
| Electrical Property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Glow wire combustion index (GWFI) | 3mm | IEC 60695-2-12 | 960 passes |
| Glow wire ignition temperature (GWIT) | 1.0mm | IEC 60695-2-13 | 825 |
| Glow wire ignition temperature (GWIT) | 3.0mm | IEC 60695-2-13 | 725 by VDE |
| UV exposure, water exposure test, and immersion | | UL 746C | F1 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | Type I, 50，屈服 | ASTM D638 | 53 Mpa |
| tensile strength | 50 mm/m，屈服 | ISO 527 | 51 Mpa |
| tensile strength | 屈服 | Internal | 48 Mpa |
| tensile strength | 50 mm/m，断裂 | ISO 527 | 40 Mpa |
| tensile strength | Type I, 50，断裂 | ASTM D638 | 43 Mpa |
| elongation | Type I, 50，屈服 | ASTM D638 | 5 |
| elongation | 50 mm/m，屈服 | ISO 527 | 4 |
| elongation at break | | ASTM D638 | 250 |
| elongation at break | Type I, 50 | ASTM D638 | 50 |
| elongation at break | 50 mm/m | ISO 527 | 42 |
| bending strength | 1.3 mm，屈服 | ASTM D790 | 80 Mpa |
| bending strength | 2 mm/m，屈服 | ISO 178 | 73 Mpa |
| Flexural modulus | 1.3 mm/m | ASTM D790 | 2200 Mpa |
| Flexural modulus | 2 mm/m | ISO 178 | 2130 Mpa |
| Tensile modulus | 5 mm/mi | ASTM D638 | 2200 Mpa |
| Tensile modulus | 1 mm/mi | ISO 527 | 2090 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | V-notch，23℃ | ISO 179/1eA | 52 kJ/m² |
| Impact strength of cantilever beam gap | 30℃ | ASTM D256 | 110 J/m |
| Impact strength of cantilever beam gap | 80*10*4，30℃ | ISO 180/1A | 8 kJ/m² |
| Impact strength of cantilever beam gap | 23℃ | ASTM D256 | 800 J/m |
| Impact strength of cantilever beam gap | 80*10*4，23℃ | ISO 180/1A | 45 kJ/m² |
| Instrumented dart impact energy -40 ℃ (-40 ℉) total energy | | ASTM D3763 | 50 J |
| Instrumented dart impact energy 23 ℃ (73 ℉) total energy | | ASTM D3763 | 50 J |